- 彎曲強度 [MPa]: 16.8
- 脆化溫度 [℃]: -14.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 37 @Temperature 100 °C | 37 @Temperature 212 °F | ML 1+4. ?Stock property.; ASTM D1646-81 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 72 | 72 | ASTM D2240-81 |
| Tensile Strength, Ultimate | 16.8 MPa | 2440 psi | ASTM D412-80 |
| Elongation at Break | 470 % | 470 % | ASTM D412-80 |
| 100% Modulus | 0.00620 GPa | 0.899 ksi | ASTM D412-80 |
| Tear Strength Test | 243 | 243 | lb-in. Graves Die C; ASTM D642-54 |
| Abrasion | 73 | 73 | NBS Abrasion Index; ASTM D1630-74. |
| Compression Set | 65 % @Temperature 70.0 °C | 65 % @Temperature 158 °F | 22 hr at 70°C. Method B. ASTM D395-69 |
| Thermal Properties | Metric | English | Comments |
| Minimum Service Temperature, Air | -14.0 °C | 6.80 °F | Brittleness Temperature |
| Brittleness Temperature | -14.0 °C | 6.80 °F | ASTM D746-79 |