- 彎曲強度 [MPa]: 17.2
- 脆化溫度 [℃]: -24.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 61 @Temperature 121 °C | 61 @Temperature 250 °F | ML-10 (gum) |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 72 | 72 | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Tensile Strength, Ultimate | 17.2 MPa | 2490 psi | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Elongation at Break | 172 % | 172 % | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Modulus of Elasticity | 0.000840 GPa | 0.122 ksi | 10% Modulus, Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| 100% Modulus | 0.00710 GPa | 1.03 ksi | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Compression Set | 30 % @Temperature 200 °C | 30 % @Temperature 392 °F | Method B, O-rings 22 hr at 200°C (Post Cured 16 hr at 232°C) |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -24.2 °C | -11.6 °F | TR-10, 100% Elongation |
| Glass Transition Temp, Tg | -24.3 °C | -11.7 °F | DSC |