| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 76 | 76 | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Tensile Strength, Ultimate | 18.0 MPa | 2610 psi | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Elongation at Break | 246 % | 246 % | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Modulus of Elasticity | 0.00102 GPa | 0.148 ksi | 10% Modulus, Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| 100% Modulus | 0.00630 GPa | 0.914 ksi | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Compression Set | 16 % @Temperature 200 °C | 16 % @Temperature 392 °F | Method B, O-rings 22 hr at 200°C (Post Cured 2 hr at 232°C) |
| Thermal Properties | Metric | English | Comments |
| Glass Transition Temp, Tg | -5.00 °C | 23.0 °F | MDSC, postcured |