| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 20 @Temperature 121 °C | 20 @Temperature 250 °F | ML-10 (gum)-Akron data |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 68 | 68 | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Tensile Strength, Ultimate | 16.2 MPa | 2350 psi | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Elongation at Break | 254 % | 254 % | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Modulus of Elasticity | 0.000700 GPa | 0.102 ksi | 10% Modulus, Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| 100% Modulus | 0.00370 GPa | 0.537 ksi | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Compression Set | 20 % @Temperature 200 °C | 20 % @Temperature 392 °F | Method B, O-rings 70 hr at 200°C (Post Cured 2 hr at 232°C) |
| Thermal Properties | Metric | English | Comments |
| Glass Transition Temp, Tg | -32.8 °C | -27.0 °F | DSC, modulated |