- 彎曲強度 [MPa]: 17.3
- 脆化溫度 [℃]: -6.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 81 @Temperature 121 °C | 81 @Temperature 250 °F | ML 1 + 10 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 77 | 77 | Cured 7 min at 177°C and Post Cured 16 hr at 200°C |
| Tensile Strength, Ultimate | 17.3 MPa | 2510 psi | Cured 7 min at 177°C and Post Cured 16 hr at 200°C |
| Elongation at Break | 213 % | 213 % | Cured 7 min at 177°C and Post Cured 16 hr at 200°C |
| 50% Modulus | 0.00360 GPa | 0.522 ksi | Cured 7 min at 177°C and Post Cured 16 hr at 200°C |
| 100% Modulus | 0.00880 GPa | 1.28 ksi | Cured 7 min at 177°C and Post Cured 16 hr at 200°C |
| Compression Set | 49 % @Temperature 200 °C | 49 % @Temperature 392 °F | Method B, O-rings 70 hr at 200°C (Post Cured 16 hr at 232°C) |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -6.00 °C | 21.2 °F | TR-10 |
| Glass Transition Temp, Tg | -11.0 °C | 12.2 °F | MDSC |