- 彎曲強度 [MPa]: 17.6
- 脆化溫度 [℃]: -30.6
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 67 | 67 | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Tensile Strength, Ultimate | 17.6 MPa | 2550 psi | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Elongation at Break | 181 % | 181 % | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Modulus of Elasticity | 0.000600 GPa | 0.0870 ksi | 10% Modulus, Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| 100% Modulus | 0.00590 GPa | 0.856 ksi | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Compression Set | 16 % @Temperature 200 °C | 16 % @Temperature 392 °F | Method B, O-rings 22 hr at 200°C (Cured 7 min at 177°C and Post Cured 16 hr at 232°C) |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -30.6 °C | -23.1 °F | TR-10 |
| Glass Transition Temp, Tg | -30.7 °C | -23.3 °F | DSC |