- 彎曲強(qiáng)度 [MPa]: 11.3
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 51 @Temperature 121 °C | 51 @Temperature 250 °F | ML 1 + 10 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 65 | 65 | Cured 10 min at 177°C and Post Cured 24 hr at 232°C |
| Tensile Strength, Ultimate | 11.3 MPa | 1640 psi | Cured 10 min at 177°C and Post Cured 24 hr at 232°C |
| Elongation at Break | 329 % | 329 % | Cured 10 min at 177°C and Post Cured 24 hr at 232°C |
| 100% Modulus | 0.00280 GPa | 0.406 ksi | Cured 10 min at 177°C and Post Cured 24 hr at 232°C |
| Compression Set | 26 % @Temperature 200 °C | 26 % @Temperature 392 °F | Method B, Plied Disks, 70 hr |