- 彎曲強度 [MPa]: 12.7
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Mooney Viscosity | 43 @Temperature 100 °C | 43 @Temperature 212 °F | ML(1+4), mu | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 61 | 61 | Cecilia 20 aged 168 hrs at 175°C | ||
| 71 | 71 | Press-cured 5 minutes at 190°C | |||
| 81 | 81 | Heat aged 2 weeks at 175°C | |||
| Tensile Strength, Ultimate | 12.7 MPa | 1840 psi | Cecilia 20 aged 168 hrs at 175°C | ||
| 13.0 MPa | 1890 psi | Heat aged 2 weeks at 175°C | |||
| 14.7 MPa | 2130 psi | Press-cured 5 minutes at 190°C | |||
| Elongation at Break | 183 % | 183 % | Heat aged 2 weeks at 175°C | ||
| 191 % | 191 % | Cecilia 20 aged 168 hrs at 175°C | |||
| 214 % | 214 % | Press-cured 5 minutes at 190°C | |||
| 100% Modulus | 0.00550 GPa | 0.798 ksi | Cecilia 20 aged 168 hrs at 175°C | ||
| 0.00700 GPa | 1.02 ksi | Press-cured 5 minutes at 190°C | |||
| 0.00790 GPa | 1.15 ksi | Heat aged 2 weeks at 175°C | |||
| Tear Strength | 5.30 kN/m | 30.2 pli | Trouser, Press-cured 5 minutes at 190°C; DIN 53508 | ||
| 21.4 kN/m | 122 pli | Press-cured 5 minutes at 190°C; ISO 34 | |||
| Compression Set | 32 % | 32 % | 70 hrs at 150°C | ||
| 75 % | 75 % | 22 hrs at 150°C; VW PV 3307 | |||
| Thermal Properties | Metric | English | Comments | ||
| Glass Transition Temp, Tg | -31.2 °C | -24.2 °F | By DSC | ||
| Descriptive Properties | |||||
| Armeen? 18D | 0.5 phr | ||||
| Bisoflex T810T | 5 phr | ||||
| Change in Volume | 13 % | Cecilia 20 aged 168 hrs at 175°C | |||
| Change in Weight | 9 % | Cecilia 20 aged 168 hrs at 175°C | |||
| DIAK No. 7(TIAC) | 2 phr | ||||
| Mooney Scorch at 121°C, t5 | 14.6 metric minutes | Time for 5 unit rise | |||
| Naugard? 445 antioxidant | 1 phr | ||||
| Perkadox 14/43 | 5 phr | ||||
| Stearic Acid | 1.5 phr | ||||
| Sterling SO-N550 black | 65 phr | ||||
| Vamac? DP | 100 phr | ||||