- 彎曲強度 [MPa]: 10.9
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Mooney Viscosity | 43.2 @Temperature 100 °C | 43.2 @Temperature 212 °F | ML(1+4), mu | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 58 | 58 | Cecilia 20 aged 168 hrs at 175°C | ||
| 71 | 71 | Press-cured 5 minutes at 190°C | |||
| 82 | 82 | Heat aged 2 weeks at 175°C | |||
| Tensile Strength, Ultimate | 10.9 MPa | 1580 psi | Cecilia 20 aged 168 hrs at 175°C | ||
| 11.7 MPa | 1700 psi | Heat aged 2 weeks at 175°C | |||
| 13.5 MPa | 1960 psi | Press-cured 5 minutes at 190°C | |||
| Elongation at Break | 273 % | 273 % | Heat aged 2 weeks at 175°C | ||
| 299 % | 299 % | Press-cured 5 minutes at 190°C | |||
| 318 % | 318 % | Cecilia 20 aged 168 hrs at 175°C | |||
| 100% Modulus | 0.00330 GPa | 0.479 ksi | Cecilia 20 aged 168 hrs at 175°C | ||
| 0.00480 GPa | 0.696 ksi | Press-cured 5 minutes at 190°C | |||
| 0.00620 GPa | 0.899 ksi | Heat aged 2 weeks at 175°C | |||
| Tear Strength | 29.0 kN/m | 165 pli | Press-cured 5 minutes at 190°C; ISO 34 | ||
| Compression Set | 35 % | 35 % | 70 hrs at 150°C | ||
| 90 % | 90 % | 22 hrs at 150°C; VW PV 3307 | |||
| Thermal Properties | Metric | English | Comments | ||
| Glass Transition Temp, Tg | -32.0 °C | -25.6 °F | By DSC | ||
| Descriptive Properties | |||||
| Armeen? 18D | 0.5 phr | ||||
| Bisoflex T810T | 5 phr | ||||
| Change in Volume | 15 % | Cecilia 20 aged 168 hrs at 175°C | |||
| Change in Weight | 10 % | Cecilia 20 aged 168 hrs at 175°C | |||
| Mooney Scorch at 121°C, t5 | 9.2 metric minutes | Time for 5 unit rise | |||
| Naugard? 445 antioxidant | 1 phr | ||||
| Perkadox 14/42 | 5 phr | ||||
| Sartomer 350(TRIM) | 2 phr | ||||
| Stearic Acid | 1.5 phr | ||||
| Sterling SO-N550 black | 65 phr | ||||
| Vamac? DP | 100 phr | ||||