- 密度 [g/cm3]: 1.58
- 吸水率 [%]: 0.11
- 缺口沖擊強度: 0.24
- 斷裂伸長率 [%]: 88.7
- 彎曲強度 [MPa]: 58.1
- 彎曲模量 [MPa]: 9.47
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in3 | ASTM D792 |
| Apparent Bulk Density | 0.620 g/cc | 0.0224 lb/in3 | Apparent density per ASTM D1895 |
| Water Absorption | 0.11 % | 0.11 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0043 cm/cm | 0.0043 in/in | ATM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 86 | 86 | ASTM D785 |
| Tensile Strength, Ultimate | 58.1 MPa | 8430 psi | ASTM D638 |
| Elongation at Break | 0.84 % | 0.84 % | ASTM D638 |
| Tensile Modulus | 8.61 GPa | 1250 ksi | ASTM D638 |
| Flexural Yield Strength | 88.7 MPa | 12900 psi | ASTM D790 |
| Flexural Modulus | 9.47 GPa | 1370 ksi | ASTM D790 |
| Compressive Yield Strength | 203 MPa | 29400 psi | ASTM D695 |
| Izod Impact, Notched | 0.240 J/cm | 0.450 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.220 J/cm2 | 1.05 ft-lb/in2 | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 2.00e+11 ohm-cm | 2.00e+11 ohm-cm | ASTM D257 |
| Dielectric Constant | 5.8 @Frequency 1e+6 Hz | 5.8 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 11.9 kV/mm | 302 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.061 @Frequency 1e+6 Hz | 0.061 @Frequency 1e+6 Hz | ASTM D150 |
| Arc Resistance | 180 sec | 180 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 205 °C | 401 °F | Heat resistance per ASTM D794 |
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 379 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.47 mm | V-0 @Thickness 0.0579 in | |