- 密度 [g/cm3]: 1.43
- 吸水率 [%]: 0.45
- 缺口沖擊強度: 0.23
- 斷裂伸長率 [%]: 83.2
- 彎曲強度 [MPa]: 55.7
- 彎曲模量 [MPa]: 7.72
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in3 | ASTM D792 |
| Apparent Bulk Density | 0.580 g/cc | 0.0210 lb/in3 | Apparent density per ASTM D1895 |
| Water Absorption | 0.45 % | 0.45 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0044 cm/cm | 0.0044 in/in | per ATM D955. Post shrinkage is 0.14% at 72hr 120oC per ASTM D1299. |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 75 | 75 | ASTM D785 |
| Tensile Strength, Ultimate | 55.7 MPa | 8080 psi | ASTM D638 |
| Elongation at Break | 0.89 % | 0.89 % | ASTM D638 |
| Tensile Modulus | 8.27 GPa | 1200 ksi | ASTM D638 |
| Flexural Yield Strength | 83.2 MPa | 12100 psi | ASTM D790 |
| Flexural Modulus | 7.72 GPa | 1120 ksi | ASTM D790 |
| Compressive Yield Strength | 155.3 MPa | 22520 psi | ASTM D695 |
| Izod Impact, Notched | 0.230 J/cm | 0.431 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.220 J/cm2 | 1.05 ft-lb/in2 | ASTM D256 |
| Impact | 150 | 150 | J/m Plenco drop ball test |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 2.128e+12 ohm-cm | 2.128e+12 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.5 @Frequency 1e+6 Hz | 4.5 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 16.2 kV/mm | 411 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.040 @Frequency 1e+6 Hz | 0.040 @Frequency 1e+6 Hz | ASTM D150 |
| Arc Resistance | 60 sec | 60 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 99.0 μm/m-°C @Temperature 20.0 °C | 55.0 μin/in-°F @Temperature 68.0 °F | |
| Thermal Conductivity | 0.370 W/m-K @Temperature 100 °C | 2.57 BTU-in/hr-ft2-°F @Temperature 212 °F | |
| Maximum Service Temperature, Air | 190 °C | 374 °F | Heat resistance per ASTM D794 |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |
- 關(guān)鍵詞:
- 供應(yīng)
- Granular
- Compression Molded
- 酚醛樹脂
- Plenco 6554 Phenolic