- 密度 [g/cm3]: 1.73
- 吸水率 [%]: 0.044
- 缺口沖擊強度: 0.173
- 彎曲強度 [MPa]: 41.0
- 彎曲模量 [MPa]: 14.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.810 g/cc | 0.0293 lb/in3 | ASTM D1895 |
| Density | 1.73 g/cc | 0.0625 lb/in3 | ASTM D792 |
| Water Absorption | 0.044 % | 0.044 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0033 cm/cm | 0.0033 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 77 | 77 | ASTM D785 |
| Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D638 |
| Elongation at Break | 0.31 % | 0.31 % | ASTM D638 |
| Tensile Modulus | 14.9 GPa | 2160 ksi | ASTM D638 |
| Flexural Strength | 87.0 MPa | 12600 psi | ASTM D790 |
| Flexural Modulus | 14.1 GPa | 2050 ksi | ASTM D790 |
| Compressive Strength | 173 MPa | 25100 psi | ASTM D695 |
| Poissons Ratio | 0.279 | 0.279 | ASTM D638 |
| Shear Modulus | 5.82 GPa | 844 ksi | Calculated |
| Izod Impact, Notched | 0.173 J/cm | 0.324 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.212 J/cm2 | 1.01 ft-lb/in2 | ASTM D256 |
| Impact | 84 | 84 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 5.80e+12 ohm-cm | 5.80e+12 ohm-cm | ASTM D247 |
| Dielectric Constant | 4.9 | 4.9 | ASTM D150 |
| Dielectric Strength | 15.6 kV/mm | 396 kV/in | Step by Step; ASTM D149 |
| 18.4 kV/mm | 467 kV/in | Short Time; ASTM D149 | |
| Dissipation Factor | 0.034 | 0.034 | ASTM D150 |
| Arc Resistance | 183 sec | 183 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 21.0 μm/m-°C @Temperature 40.0 - 130 °C | 11.7 μin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Maximum Service Temperature, Air | 216 °C | 421 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | |
| Oxygen Index | 43 % | 43 % | ASTM D2863 |
| Shrinkage | 0.047 % | 0.047 % | 72 hr, 120oC; ASTM D1299 |