- 密度 [g/cm3]: 1.39
- 吸水率 [%]: 0.38
- 缺口沖擊強(qiáng)度: 0.173
- 彎曲強(qiáng)度 [MPa]: 62.0
- 彎曲模量 [MPa]: 8.40
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.600 g/cc | 0.0217 lb/in3 | ASTM D1895 |
| Density | 1.39 g/cc | 0.0502 lb/in3 | ASTM D792 |
| Water Absorption | 0.38 % | 0.38 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0047 cm/cm | 0.0047 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 93 | 93 | ASTM D785 |
| Tensile Strength, Ultimate | 62.0 MPa | 8990 psi | ASTM D638 |
| Elongation at Break | 0.79 % | 0.79 % | ASTM D638 |
| Tensile Modulus | 9.00 GPa | 1310 ksi | ASTM D638 |
| Flexural Strength | 97.0 MPa | 14100 psi | ASTM D790 |
| Flexural Modulus | 8.40 GPa | 1220 ksi | ASTM D790 |
| Compressive Strength | 227 MPa | 32900 psi | ASTM D695 |
| Izod Impact, Notched | 0.173 J/cm | 0.324 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.190 J/cm2 | 0.904 ft-lb/in2 | ASTM D256 |
| Impact | 115 | 115 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.20e+12 ohm-cm | 2.20e+12 ohm-cm | ASTM D247 |
| Dielectric Constant | 4.8 | 4.8 | ASTM D150 |
| Dielectric Strength | 15.5 kV/mm | 394 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.039 | 0.039 | ASTM D150 |
| Arc Resistance | 98 sec | 98 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 76.0 μm/m-°C @Temperature 40.0 - 130 °C | 42.2 μin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 0.360 W/m-K @Temperature 100 °C | 2.50 BTU-in/hr-ft2-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 202 °C | 396 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 168 °C | 334 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |
| Oxygen Index | 25.5 % | 25.5 % | ASTM D2863 |
| Shrinkage | 0.173 % | 0.173 % | 72 hr, 120oC; ASTM D1299 |