- 密度 [g/cm3]: 1.41
- 吸水率 [%]: 0.273
- 缺口沖擊強度: 0.189
- 彎曲強度 [MPa]: 61.0
- 彎曲模量 [MPa]: 7.60
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.640 g/cc | 0.0231 lb/in3 | ASTM D1895 |
| Density | 1.41 g/cc | 0.0509 lb/in3 | ASTM D792 |
| Water Absorption | 0.273 % | 0.273 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 86 | 86 | ASTM D785 |
| Tensile Strength, Ultimate | 61.0 MPa | 8850 psi | ASTM D638 |
| Elongation at Break | 0.83 % | 0.83 % | ASTM D638 |
| Tensile Modulus | 8.70 GPa | 1260 ksi | ASTM D638 |
| Flexural Strength | 90.0 MPa | 13100 psi | ASTM D790 |
| Flexural Modulus | 7.60 GPa | 1100 ksi | ASTM D790 |
| Compressive Strength | 190 MPa | 27600 psi | ASTM D695 |
| Poissons Ratio | 0.35 | 0.35 | ASTM D638 |
| Shear Modulus | 3.22 GPa | 467 ksi | Calculated |
| Izod Impact, Notched | 0.189 J/cm | 0.354 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.190 J/cm2 | 0.904 ft-lb/in2 | ASTM D256 |
| Impact | 104 | 104 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.20e+12 ohm-cm | 1.20e+12 ohm-cm | ASTM D247 |
| Dielectric Constant | 4.6 | 4.6 | ASTM D150 |
| Dielectric Strength | 13.0 kV/mm | 330 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.045 | 0.045 | ASTM D150 |
| Arc Resistance | 138 sec | 138 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 48.0 μm/m-°C @Temperature 40.0 - 130 °C | 26.7 μin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 0.400 W/m-K @Temperature 100 °C | 2.78 BTU-in/hr-ft2-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 200 °C | 392 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 155 °C | 311 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |
| Oxygen Index | 24.5 % | 24.5 % | ASTM D2863 |
| Shrinkage | 0.274 % | 0.274 % | 72 hr, 120oC; ASTM D1299 |