- 密度 [g/cm3]: 1.39
- 吸水率 [%]: 0.32
- 缺口沖擊強度: 0.181
- 彎曲強度 [MPa]: 54.0
- 彎曲模量 [MPa]: 7.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.600 g/cc | 0.0217 lb/in3 | ASTM D1895 |
| Density | 1.39 g/cc | 0.0502 lb/in3 | ASTM D792 |
| Water Absorption | 0.32 % | 0.32 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0065 cm/cm | 0.0065 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 91 | 91 | ASTM D785 |
| Tensile Strength, Ultimate | 54.0 MPa | 7830 psi | ASTM D638 |
| Elongation at Break | 0.67 % | 0.67 % | ASTM D638 |
| Tensile Modulus | 7.80 GPa | 1130 ksi | ASTM D638 |
| Flexural Strength | 81.0 MPa | 11700 psi | ASTM D790 |
| Flexural Modulus | 7.10 GPa | 1030 ksi | ASTM D790 |
| Compressive Strength | 214 MPa | 31000 psi | ASTM D695 |
| Poissons Ratio | 0.35 | 0.35 | ASTM D638 |
| Shear Modulus | 2.89 GPa | 419 ksi | Calculated |
| Izod Impact, Notched | 0.181 J/cm | 0.339 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.195 J/cm2 | 0.928 ft-lb/in2 | ASTM D256 |
| Impact | 98 | 98 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.70e+11 ohm-cm | 2.70e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 6.1 | 6.1 | ASTM D150 |
| Dielectric Strength | 8.60 kV/mm | 218 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.065 | 0.065 | ASTM D150 |
| Arc Resistance | 117 sec | 117 sec | ASTM D495 |
| Comparative Tracking Index | 150 V | 150 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 197 °C | 387 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 351 °F | ASTM D648 |
| Flammability, UL94 | V-1 @Thickness 1.50 mm | V-1 @Thickness 0.0591 in | |
| Oxygen Index | 27 % | 27 % | ASTM D2863 |
| Shrinkage | 0.21 % | 0.21 % | 72 hr, 120oC; ASTM D1299 |