- 密度 [g/cm3]: 1.4
- 吸水率 [%]: 0.47
- 缺口沖擊強度: 0.152
- 彎曲強度 [MPa]: 62.0
- 彎曲模量 [MPa]: 7.40
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.610 g/cc | 0.0220 lb/in3 | ASTM D1895 |
| Density | 1.40 g/cc | 0.0506 lb/in3 | ASTM D792 |
| Water Absorption | 0.47 % | 0.47 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0041 cm/cm | 0.0041 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 84 | 84 | ASTM D785 |
| Tensile Strength, Ultimate | 62.0 MPa | 8990 psi | ASTM D638 |
| Elongation at Break | 0.87 % | 0.87 % | ASTM D638 |
| Tensile Modulus | 8.00 GPa | 1160 ksi | ASTM D638 |
| Flexural Strength | 91.0 MPa | 13200 psi | ASTM D790 |
| Flexural Modulus | 7.40 GPa | 1070 ksi | ASTM D790 |
| Compressive Strength | 215 MPa | 31200 psi | ASTM D695 |
| Izod Impact, Notched | 0.152 J/cm | 0.285 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.187 J/cm2 | 0.890 ft-lb/in2 | ASTM D256 |
| Impact | 102 | 102 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 3.00e+13 ohm-cm | 3.00e+13 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.4 | 5.4 | ASTM D150 |
| Dielectric Strength | 9.50 kV/mm | 241 kV/in | Step by Step; ASTM D149 |
| 12.9 kV/mm | 328 kV/in | Short Time; ASTM D149 | |
| Dissipation Factor | 0.041 | 0.041 | ASTM D150 |
| Arc Resistance | 87 sec | 87 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 63.0 μm/m-°C @Temperature 40.0 - 130 °C | 35.0 μin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 0.370 W/m-K @Temperature 100 °C | 2.57 BTU-in/hr-ft2-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 203 °C | 397 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |
| Oxygen Index | 29 % | 29 % | ASTM D2863 |
| Shrinkage | 0.40 % | 0.40 % | 72 hr, 120oC; ASTM D1299 |