- 密度 [g/cm3]: 1.38
- 吸水率 [%]: 0.41
- 缺口沖擊強度: 0.186
- 彎曲強度 [MPa]: 56.0
- 彎曲模量 [MPa]: 6.90
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.610 g/cc | 0.0220 lb/in3 | ASTM D1895 |
| Density | 1.38 g/cc | 0.0499 lb/in3 | ASTM D792 |
| Water Absorption | 0.41 % | 0.41 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0107 cm/cm | 0.0107 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 85 | 85 | ASTM D785 |
| Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ASTM D638 |
| Elongation at Break | 0.83 % | 0.83 % | ASTM D638 |
| Tensile Modulus | 7.80 GPa | 1130 ksi | ASTM D638 |
| Flexural Strength | 81.0 MPa | 11700 psi | ASTM D790 |
| Flexural Modulus | 6.90 GPa | 1000 ksi | ASTM D790 |
| Compressive Strength | 202 MPa | 29300 psi | ASTM D695 |
| Poissons Ratio | 0.36 | 0.36 | ASTM D638 |
| Shear Modulus | 2.87 GPa | 416 ksi | Calculated |
| Izod Impact, Notched | 0.186 J/cm | 0.348 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.186 J/cm2 | 0.885 ft-lb/in2 | ASTM D256 |
| Impact | 103 | 103 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.30e+11 ohm-cm | 2.30e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 4.8 | 4.8 | ASTM D150 |
| Dielectric Strength | 10.2 kV/mm | 259 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.057 | 0.057 | ASTM D150 |
| Arc Resistance | 126 sec | 126 sec | ASTM D495 |
| Comparative Tracking Index | 150 V | 150 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 43.0 μm/m-°C @Temperature 40.0 - 130 °C | 23.9 μin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Maximum Service Temperature, Air | 196 °C | 385 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |
| Oxygen Index | 26.1 % | 26.1 % | ASTM D2863 |
| Shrinkage | 0.44 % | 0.44 % | 72 hr, 120oC; ASTM D1299 |