- 密度 [g/cm3]: 1.6
- 吸水率 [%]: 0.36
- 缺口沖擊強度: 0.201
- 彎曲強度 [MPa]: 56.0
- 彎曲模量 [MPa]: 8.90
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.580 g/cc | 0.0210 lb/in3 | ASTM D1895 |
| Density | 1.60 g/cc | 0.0578 lb/in3 | ASTM D792 |
| Water Absorption | 0.36 % | 0.36 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0042 cm/cm | 0.0042 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 71 | 71 | ASTM D785 |
| Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ASTM D638 |
| Elongation at Break | 0.64 % | 0.64 % | ASTM D638 |
| Tensile Modulus | 10.0 GPa | 1450 ksi | ASTM D638 |
| Flexural Strength | 89.0 MPa | 12900 psi | ASTM D790 |
| Flexural Modulus | 8.90 GPa | 1290 ksi | ASTM D790 |
| Compressive Strength | 165 MPa | 23900 psi | ASTM D695 |
| Izod Impact, Notched | 0.201 J/cm | 0.377 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.221 J/cm2 | 1.05 ft-lb/in2 | ASTM D256 |
| Impact | 148 | 148 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.80e+13 ohm-cm | 1.80e+13 ohm-cm | ASTM D247 |
| Dielectric Constant | 6.5 | 6.5 | ASTM D150 |
| Dielectric Strength | 8.50 kV/mm | 216 kV/in | Step by Step; ASTM D149 |
| 12.0 kV/mm | 305 kV/in | Short Time; ASTM D149 | |
| Dissipation Factor | 0.054 | 0.054 | ASTM D150 |
| Arc Resistance | 186 sec | 186 sec | ASTM D495 |
| Comparative Tracking Index | 425 V | 425 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 0.580 W/m-K @Temperature 100 °C | 4.03 BTU-in/hr-ft2-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 152 °C | 306 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 184 °C | 363 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | |
| Oxygen Index | 33 % | 33 % | ASTM D2863 |
| Shrinkage | 0.89 % | 0.89 % | 240 hr, 105oC; ASTM D1299 |