- 密度 [g/cm3]: 1.59
- 吸水率 [%]: 0.46
- 缺口沖擊強度: 0.168
- 彎曲強度 [MPa]: 65.0
- 彎曲模量 [MPa]: 8.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.660 g/cc | 0.0238 lb/in3 | ASTM D1895 |
| Density | 1.59 g/cc | 0.0574 lb/in3 | ASTM D792 |
| Water Absorption | 0.46 % | 0.46 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0093 cm/cm | 0.0093 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 85 | 85 | ASTM D785 |
| Tensile Strength, Ultimate | 65.0 MPa | 9430 psi | ASTM D638 |
| Elongation at Break | 0.89 % | 0.89 % | ASTM D638 |
| Tensile Modulus | 9.00 GPa | 1310 ksi | ASTM D638 |
| Flexural Strength | 97.0 MPa | 14100 psi | ASTM D790 |
| Flexural Modulus | 8.10 GPa | 1170 ksi | ASTM D790 |
| Compressive Strength | 194 MPa | 28100 psi | ASTM D695 |
| Poissons Ratio | 0.36 | 0.36 | ASTM D638 |
| Shear Modulus | 3.31 GPa | 480 ksi | Calculated |
| Izod Impact, Notched | 0.168 J/cm | 0.315 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.216 J/cm2 | 1.03 ft-lb/in2 | ASTM D256 |
| Impact | 106 | 106 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 9.70e+12 ohm-cm | 9.70e+12 ohm-cm | ASTM D247 |
| Dielectric Constant | 7.7 | 7.7 | ASTM D150 |
| Dielectric Strength | 6.00 kV/mm | 152 kV/in | Step by Step; ASTM D149 |
| 9.20 kV/mm | 234 kV/in | Short Time; ASTM D149 | |
| Dissipation Factor | 0.064 | 0.064 | ASTM D150 |
| Arc Resistance | 185 sec | 185 sec | ASTM D495 |
| Comparative Tracking Index | 600 V | 600 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 53.0 μm/m-°C @Temperature 40.0 - 130 °C | 29.4 μin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Maximum Service Temperature, Air | 140 °C | 284 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 186 °C | 367 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.610 mm | V-0 @Thickness 0.0240 in | |
| Oxygen Index | 33 % | 33 % | ASTM D2863 |
| Shrinkage | 1.24 % | 1.24 % | 240 hr, 105oC; ASTM D1299 |