- 密度 [g/cm3]: 1.68
- 吸水率 [%]: 0.12
- 缺口沖擊強度: 0.15
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.68 - 1.78 g/cc | 0.0607 - 0.0643 lb/in3 | Molding; IS 867-1963 | ||
| Apparent Bulk Density | 0.700 - 0.850 g/cc | 0.0253 - 0.0307 lb/in3 | IS 867-1963 | ||
| Water Absorption | 0.12 - 0.25 % | 0.12 - 0.25 % | IS 13411-1993 | ||
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | IS 13411-1992 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 30.0 - 45.0 MPa | 4350 - 6530 psi | 5 mm/min.; IS 867-1963 | ||
| Shear Strength | 50.0 - 65.0 MPa | 7250 - 9430 psi | IS 867-1963 | ||
| Izod Impact, Notched | 0.150 - 0.250 J/cm | 0.281 - 0.468 ft-lb/in | IS 13411-1992 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+12 - 1.00e+13 ohm-cm | 1.00e+12 - 1.00e+13 ohm-cm | IS 3396-1979 | ||
| Surface Resistance | 3.16228e+11 - 1.00e+12 ohm | 3.16228e+11 - 1.00e+12 ohm | IS 3396-1979 | ||
| Dielectric Strength | 8.00 - 10.5 kV/mm @Temperature 90.0 °C | 203 - 267 kV/in @Temperature 194 °F | IS 2584-1963 | ||
| Processing Properties | Metric | English | Comments | ||
| Mold Temperature | 160 - 180 °C | 320 - 356 °F | |||
| Injection Pressure | 14.7 - 35.28 MPa | 2130 - 5117 psi | Mold Pressure | ||
| Cure Time | 0.917 - 1.08 min | 0.0153 - 0.0181 hour | per mm | ||
| Shelf Life | 12.0 Month | 12.0 Month | 10-25°C | ||
| Descriptive Properties | |||||
| Chloride Content | Nil to traces | ||||
| Free Phenol | Nil to traces | ||||