- 密度 [g/cm3]: 1.8
- 吸水率 [%]: 0.1
- 缺口沖擊強度: 0.48
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.80 - 1.85 g/cc | 0.0650 - 0.0668 lb/in3 | Molding; IS 867-1963 | ||
| Apparent Bulk Density | 0.750 - 0.850 g/cc | 0.0271 - 0.0307 lb/in3 | IS 867-1963 | ||
| Water Absorption | 0.10 - 0.20 % | 0.10 - 0.20 % | IS 13411-1993 | ||
| Linear Mold Shrinkage | 0.00050 - 0.0020 cm/cm | 0.00050 - 0.0020 in/in | IS 13411-1992 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | >= 60.0 MPa | >= 8700 psi | 5 mm/min.; IS 867-1963 | ||
| Shear Strength | >= 110 MPa | >= 16000 psi | 2mm/min.; IS 867-1963 | ||
| Izod Impact, Notched | >= 0.480 J/cm | >= 0.899 ft-lb/in | IS 13411-1992 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+12 - 1.0 ohm-cm | 1.00e+12 - 1.0 ohm-cm | IS 3396-1979 | ||
| Surface Resistance | 1.00e+11 - 1.0 ohm | 1.00e+11 - 1.0 ohm | IS 3396-1979 | ||
| Dielectric Strength | >= 10.0 kV/mm @Temperature 90.0 °C | >= 254 kV/in @Temperature 194 °F | IS 2584-1963 | ||
| Comparative Tracking Index | >= 175 V | >= 175 V | 2824-1975 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 230 °C | 446 °F | 2 hours | ||
| Processing Properties | Metric | English | Comments | ||
| Mold Temperature | 160 - 180 °C | 320 - 356 °F | |||
| Injection Pressure | 15.68 - 34.3 MPa | 2274 - 4970 psi | Mold Pressure | ||
| Cure Time | 0.833 - 1.17 min | 0.0139 - 0.0194 hour | per mm | ||
| Shelf Life | 4.00 Month | 4.00 Month | 10-25°C | ||
| Descriptive Properties | |||||
| Ammonia content | Nil | ||||