- 密度 [g/cm3]: 1.32
- 吸水率 [%]: 0.2
- 缺口沖擊強(qiáng)度: 0.22
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 - 1.38 g/cc | 0.0477 - 0.0499 lb/in3 | Molding; IS 867-1963 |
| Apparent Bulk Density | 0.600 - 0.660 g/cc | 0.0217 - 0.0238 lb/in3 | IS 867-1963 |
| Water Absorption | 0.20 - 0.40 % | 0.20 - 0.40 % | IS 13411-1993 |
| Linear Mold Shrinkage | 0.0070 - 0.010 cm/cm | 0.0070 - 0.010 in/in | IS 13411-1992 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 46.0 - 53.0 MPa | 6670 - 7690 psi | 5 mm/min.; IS 867-1963 |
| Shear Strength | 67.0 - 77.0 MPa | 9720 - 11200 psi | IS 867-1963 |
| Izod Impact, Notched | 0.220 - 0.300 J/cm | 0.412 - 0.562 ft-lb/in | IS 13411-1992 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+11 - 1.00e+12 ohm-cm | 1.00e+11 - 1.00e+12 ohm-cm | IS 3396-1979 |
| Surface Resistance | 3.2e+10 - 3.2e+11 ohm | 3.2e+10 - 3.2e+11 ohm | IS 3396-1979 |
| Dielectric Strength | 6.00 - 8.00 kV/mm @Temperature 90.0 °C | 152 - 203 kV/in @Temperature 194 °F | IS 2584-1963 |
| Comparative Tracking Index | >= 135 V | >= 135 V | 2824-1975 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 65.0 - 85.0 °C | 149 - 185 °F | |
| Front Barrel Temperature | 85.0 - 95.0 °C | 185 - 203 °F | |
| Nozzle Temperature | <= 105 °C | <= 221 °F | |
| Mold Temperature | 160 - 180 °C | 320 - 356 °F | |
| Injection Pressure | 98.0 - 196 MPa | 14200 - 28400 psi | |
| Hold Pressure | 58.8 MPa | 8530 psi | |
| Cure Time | 0.200 - 0.333 min | 0.00333 - 0.00556 hour | per mm |
| Shelf Life | 12.0 Month | 12.0 Month | 10-25°C |