- 密度 [g/cm3]: 1.44
- 吸水率 [%]: 0.2
- 缺口沖擊強度: 0.25
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 - 1.53 g/cc | 0.0520 - 0.0553 lb/in3 | Molding; IS 867-1963 |
| Apparent Bulk Density | 0.690 - 0.720 g/cc | 0.0249 - 0.0260 lb/in3 | IS 867-1963 |
| Water Absorption | 0.20 - 0.30 % | 0.20 - 0.30 % | IS 13411-1993 |
| Linear Mold Shrinkage | 0.0050 - 0.0065 cm/cm | 0.0050 - 0.0065 in/in | Compression specimen; IS 13411-1992 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 42.0 - 58.0 MPa | 6090 - 8410 psi | 5 mm/min.; IS 867-1963 |
| Shear Strength | 55.0 - 70.0 MPa | 7980 - 10200 psi | IS 867-1963 |
| Izod Impact, Notched | 0.250 - 0.350 J/cm | 0.468 - 0.656 ft-lb/in | IS 13411-1992 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 3.16228e+10 - 1.00e+11 ohm-cm | 3.16228e+10 - 1.00e+11 ohm-cm | IS 3396-1979 |
| Surface Resistance | 3.16228e+9 - 1.00e+10 ohm | 3.16228e+9 - 1.00e+10 ohm | IS 3396-1979 |
| Dielectric Strength | 4.00 - 5.50 kV/mm @Temperature 90.0 °C | 102 - 140 kV/in @Temperature 194 °F | IS 2584-1963 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | >= 200 °C | >= 392 °F | 2 hours |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 160 - 180 °C | 320 - 356 °F | |
| Injection Pressure | 15.68 - 34.3 MPa | 2274 - 4970 psi | Mold Pressure |
| Cure Time | 0.783 - 0.917 min | 0.0131 - 0.0153 hour | per mm |
| Shelf Life | 12.0 Month | 12.0 Month | 10-25°C |