- 密度 [g/cm3]: 1.7
- 吸水率 [%]: 0.15
- 缺口沖擊強度: 0.4
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.70 - 1.76 g/cc | 0.0614 - 0.0636 lb/in3 | Molding; IS 867-1963 |
| Apparent Bulk Density | 0.750 - 0.850 g/cc | 0.0271 - 0.0307 lb/in3 | IS 867-1963 |
| Water Absorption | 0.15 - 0.20 % | 0.15 - 0.20 % | IS 13411-1993 |
| Linear Mold Shrinkage | 0.0025 - 0.0040 cm/cm | 0.0025 - 0.0040 in/in | IS 13411-1992 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 53.0 - 60.0 MPa | 7690 - 8700 psi | 5 mm/min.; IS 867-1963 |
| Shear Strength | 75.0 - 80.0 MPa | 10900 - 11600 psi | IS 867-1963 |
| Izod Impact, Notched | 0.400 - 0.500 J/cm | 0.749 - 0.937 ft-lb/in | IS 13411-1992 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 3.2e+11 - 3.2e+12 ohm-cm | 3.2e+11 - 3.2e+12 ohm-cm | IS 3396-1979 |
| Surface Resistance | 1.00e+11 - 1.00e+12 ohm | 1.00e+11 - 1.00e+12 ohm | IS 3396-1979 |
| Dielectric Strength | >= 9.00 kV/mm @Temperature 90.0 °C | >= 229 kV/in @Temperature 194 °F | IS 2584-1963 |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 160 - 180 °C | 320 - 356 °F | |
| Injection Pressure | 15.68 - 34.3 MPa | 2274 - 4970 psi | Mold Pressure |
| Cure Time | 0.833 - 1.00 min | 0.0139 - 0.0167 hour | per mm |
| Shelf Life | 12.0 Month | 12.0 Month | 10-25°C |