Momentive Performance Materials PF 13 Phenolic Formaldehyde Resin, UL Listed

Momentive Performance Materials PF 13 Phenolic Formaldehyde Resin, UL Listed 物性表: Momentive Performance Materials PF 13 Phenolic Formaldehyde Resin, UL Listed物性表及特性介紹,Momentive Performance Materials PF 13 Phenolic Formaldehyde Resin, UL Listed注塑參數(shù)詳情,如需Momentive Performance Materials PF 13 Phenolic Formaldehyde Resin, UL Listed下載, 可到相關(guān)下載區(qū)下載

密度 [g/cm3]: 1.85
彎曲模量 [MPa]: 25.0

Physical Properties	Metric	English	Comments

Density	1.85 g/cc	0.0668 lb/in3	ISO 1183
Apparent Bulk Density	0.650 g/cc	0.0235 lb/in3	ISO 60
Linear Mold Shrinkage, Flow	-0.000100 cm/cm	-0.000100 in/in	Compression molding; ISO 2577

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	425 MPa	61600 psi	H 961/30; ISO 2039/P1
Flexural Strength	85.0 MPa	12300 psi	2 mm/min; ISO 178
Flexural Modulus	25.0 GPa	3630 ksi	ISO 178
Compressive Strength	135 MPa	19600 psi	Test specimen flat tested; ISO 604
Charpy Impact Unnotched	0.300 J/cm2 @Temperature 23.0 °C	1.43 ft-lb/in2 @Temperature 73.4 °F	ISO 179-1/2 eU
Charpy Impact, Notched	0.200 J/cm2 @Temperature 23.0 °C	0.952 ft-lb/in2 @Temperature 73.4 °F	ISO 179-1/2 eA

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+12 ohm-cm	1.00e+12 ohm-cm	IEC 60093
Surface Resistance	1.00e+11 ohm	1.00e+11 ohm	IEC 60093
Dielectric Constant	5.0 @Frequency 100 Hz	5.0 @Frequency 100 Hz	IEC 60250
Dielectric Strength	30.0 kV/mm @Thickness 1.00 mm	762 kV/in @Thickness 0.0394 in	IEC 60243-P1
Dissipation Factor	0.040 @Frequency 100 Hz	0.040 @Frequency 100 Hz	IEC 60250
Arc Resistance	180 - 240 sec @Thickness 3.00 mm	180 - 240 sec @Thickness 0.118 in	(NC)
High Voltage Arc Resistance to Ignition (HVAR)	>= 300 sec @Thickness 0.750 mm	>= 300 sec @Thickness 0.0295 in	NC
Comparative Tracking Index	175 V	175 V	Test liquid A; IEC 60112
Hot Wire Ignition, HWI	30 - 60 sec @Thickness 0.750 mm	30 - 60 sec @Thickness 0.0295 in	NC
	>= 120 sec @Thickness 1.50 mm	>= 120 sec @Thickness 0.0591 in	NC
High Amp Arc Ignition, HAI	30 - 60 arcs @Thickness 0.750 mm	30 - 60 arcs @Thickness 0.0295 in	NC
High Voltage Arc-Tracking Rate, HVTR	0.000 - 10.0 mm/min @Thickness 3.00 mm	0.000 - 0.394 in/min @Thickness 0.118 in	(NC)

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	150 °C	302 °F	<20000 hours; IEC 60216-P1
	200 °C	392 °F	< 50 hours; IEC 60216-P1
Deflection Temperature at 8.0 MPa	160 °C	320 °F	ISO 75-2
UL RTI, Electrical	150 °C @Thickness 0.750 mm	302 °F @Thickness 0.0295 in	NC
UL RTI, Mechanical with Impact	150 °C @Thickness 0.750 mm	302 °F @Thickness 0.0295 in	NC
UL RTI, Mechanical without Impact	150 °C @Thickness 0.750 mm	302 °F @Thickness 0.0295 in	NC
Flammability, UL94	V-1 @Thickness 0.750 mm	V-1 @Thickness 0.0295 in	NC
	V-0 @Thickness 3.00 mm	V-0 @Thickness 0.118 in	(NC)
Shrinkage	0.020 %	0.020 %	Compression molding, 168 hours/110°C; ISO 2577

Processing Properties	Metric	English	Comments
Feed Temperature	60.0 - 75.0 °C	140 - 167 °F	Injection molding
Nozzle Temperature	80.0 - 100 °C	176 - 212 °F	Injection molding
Melt Temperature	80.0 - 100 °C	176 - 212 °F	Injection molding
Mold Temperature	160 - 190 °C	320 - 374 °F	Injection molding
	160 - 190 °C	320 - 374 °F	Compression molding
Injection Pressure	>= 15.0 MPa	>= 2180 psi	Compression and injection cavity mold pressure
Back Pressure	0.500 - 2.00 MPa	72.5 - 290 psi	Injection molding
Cure Time	0.167 - 0.333 min	0.00278 - 0.00556 hour	Per 1 mm of wall thickness, injection molding
	0.333 - 0.667 min	0.00556 - 0.0111 hour	Per 1 mm of wall thickness, compression molding

Descriptive Properties
Chromatic Spectrum	All Colors
Creep Rupture Strength	Very Good
Holding Pressure	Approximately 40-60% of injection pressure
Media Resistance	Very Good
Moisture Absorption	10 mg		ISO 62, 24 hours at 23°C
Reserves by Peak Temperature	Very High
Thermal Expansion	Very Slight

關(guān)鍵詞:
供應(yīng)
酚醛樹脂
Momentive Performance Materials PF 13 Phenolic Formaldehyde Resin
UL Listed

轉(zhuǎn)載請注明: 轉(zhuǎn)自中國塑膠原料之家 http://www.spnmy.cn/wuxingbiao/

本文鏈接: http://www.spnmy.cn/yuanliaoku/show-34837.html

免責(zé)聲明: 本文 Momentive Performance Materials PF 13 Phenolic Formaldehyde Resin, UL Listed 僅代表作者個人觀點(diǎn)，中國塑膠原料之家無關(guān)。中國塑膠原料之家網(wǎng)所轉(zhuǎn)載的內(nèi)容，其版權(quán)均由原作者和資料提供方所擁有！如因作品版權(quán)問題需要處理，請與我們聯(lián)絡(luò)