- 密度 [g/cm3]: 1.4
- 吸水率 [%]: 0.5
- 彎曲強度 [MPa]: 48.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in3 | ASTM D792 |
| Apparent Bulk Density | 0.580 g/cc | 0.0210 lb/in3 | ASTM D1895 |
| Water Absorption | 0.50 % | 0.50 % | ASTM D570 |
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 48.0 MPa | 6960 psi | ASTM D638 |
| Tensile Modulus | 8.30 GPa | 1200 ksi | ASTM D638 |
| Flexural Strength | 69.0 MPa | 10000 psi | |
| Compressive Strength | 207 MPa | 30000 psi | ASTM D695 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | ASTM D257 |
| Dielectric Constant | 5.5 @Frequency 1e+6 Hz | 5.5 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 6.90 kV/mm | 175 kV/in | Step by step; ASTM D149 |
| 8.80 kV/mm | 224 kV/in | Short Time; ASTM D149 | |
| Dissipation Factor | 0.060 @Frequency 1e+6 Hz | 0.060 @Frequency 1e+6 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 150 °C | 302 °F | UL temperature Index |
| Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |
| V-1 @Thickness 3.00 mm | V-1 @Thickness 0.118 in | ||