- 密度 [g/cm3]: 1.05
- 吸水率 [%]: 0.28
- 缺口沖擊強度: 0.27
- 斷裂伸長率 [%]: 55.0
- 彎曲強度 [MPa]: 38.0
- 彎曲模量 [MPa]: 4.80
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 - 1.45 g/cc | 0.0379 - 0.0524 lb/in3 | Average value: 1.33 g/cc Grade Count:26 |
| Water Absorption | 0.280 - 1.90 % | 0.280 - 1.90 % | Average value: 0.883 % Grade Count:8 |
| Linear Mold Shrinkage | 0.00200 - 0.00400 cm/cm | 0.00200 - 0.00400 in/in | Average value: 0.00300 cm/cm Grade Count:7 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 70.0 - 115 | 70.0 - 115 | Average value: 94.0 Grade Count:7 |
| Tensile Strength, Ultimate | 38.0 - 120 MPa | 5510 - 17400 psi | Average value: 64.6 MPa Grade Count:17 |
| Flexural Yield Strength | 55.0 - 135 MPa | 7980 - 19600 psi | Average value: 90.0 MPa Grade Count:25 |
| Flexural Modulus | 4.80 - 11.0 GPa | 696 - 1600 ksi | Average value: 7.41 GPa Grade Count:17 |
| Compressive Yield Strength | 70.0 - 300 MPa | 10200 - 43500 psi | Average value: 180 MPa Grade Count:25 |
| Shear Strength | 10.0 - 20.0 MPa | 1450 - 2900 psi | Average value: 15.0 MPa Grade Count:8 |
| Izod Impact, Notched | 0.270 - 0.630 J/cm | 0.506 - 1.18 ft-lb/in | Average value: 0.447 J/cm Grade Count:9 |
| Electrical Properties | Metric | English | Comments |
| Insulation Resistance | 100000 - 1.00e+10 ohm | 100000 - 1.00e+10 ohm | Average value: 9.46e+8 ohm Grade Count:14 |
| Dielectric Constant | 5.50 - 6.00 | 5.50 - 6.00 | Average value: 5.67 Grade Count:6 |
| Dielectric Strength | 1.00 - 14.6 kV/mm | 25.4 - 371 kV/in | Average value: 5.72 kV/mm Grade Count:7 |
| Dielectric Breakdown | >= 20000 V @Temperature 90.0 - 90.0 °C | >= 20000 V @Temperature 194 - 194 °F | Average value: 23300 V Grade Count:6 |
| >= 10000 V @Temperature 90.0 - 90.0 °C | >= 10000 V @Temperature 194 - 194 °F | Average value: 23300 V Grade Count:8 | |
| >= 10000 V @Time 20.0 - 60.0 sec | >= 10000 V @Time 0.00556 - 0.0167 hour | Average value: 23300 V Grade Count:8 | |
| Dissipation Factor | 0.0500 - 0.0550 | 0.0500 - 0.0550 | Average value: 0.0517 Grade Count:6 |
| Arc Resistance | 60.0 - 120 sec | 60.0 - 120 sec | Average value: 83.0 sec Grade Count:5 |
| Comparative Tracking Index | 100 V | 100 V | Average value: 100 V Grade Count:8 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 24.0 - 47.0 μm/m-°C | 13.3 - 26.1 μin/in-°F | Average value: 33.4 μm/m-°C Grade Count:5 |
| CTE, linear, Transverse to Flow | 52.0 - 69.0 μm/m-°C | 28.9 - 38.3 μin/in-°F | Average value: 58.0 μm/m-°C Grade Count:3 |
| Thermal Conductivity | 0.540 - 0.580 W/m-K | 3.75 - 4.03 BTU-in/hr-ft2-°F | Average value: 0.560 W/m-K Grade Count:3 |
| Maximum Service Temperature, Air | 150 °C | 302 °F | Average value: 150 °C Grade Count:4 |
| Deflection Temperature at 1.8 MPa (264 psi) | 165 - 238 °C | 329 - 460 °F | Average value: 189 °C Grade Count:9 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:7 |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 155 - 180 °C | 311 - 356 °F | Average value: 168 °C Grade Count:3 |