- 密度 [g/cm3]: 1.49
- 吸水率 [%]: 0.03
- 缺口沖擊強(qiáng)度: 0.209
- 斷裂伸長(zhǎng)率 [%]: 75.0
- 彎曲強(qiáng)度 [MPa]: 34.0
- 彎曲模量 [MPa]: 8.60
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 - 2.12 g/cc | 0.0538 - 0.0766 lb/in3 | Average value: 1.79 g/cc Grade Count:64 |
| Apparent Bulk Density | 0.770 - 1.02 g/cc | 0.0278 - 0.0368 lb/in3 | Average value: 0.878 g/cc Grade Count:5 |
| Water Absorption | 0.0300 - 1.81 % | 0.0300 - 1.81 % | Average value: 0.123 % Grade Count:48 |
| Linear Mold Shrinkage | 0.000500 - 0.00670 cm/cm | 0.000500 - 0.00670 in/in | Average value: 0.00238 cm/cm Grade Count:58 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 78.0 - 100 | 78.0 - 100 | Average value: 90.4 Grade Count:15 |
| Hardness, Rockwell M | 85.0 - 120 | 85.0 - 120 | Average value: 105 Grade Count:9 |
| Tensile Strength, Ultimate | 34.0 - 138 MPa | 4930 - 20000 psi | Average value: 76.7 MPa Grade Count:62 |
| Elongation at Break | 0.500 - 1.60 % | 0.500 - 1.60 % | Average value: 0.931 % Grade Count:21 |
| Modulus of Elasticity | 9.30 - 25.5 GPa | 1350 - 3700 ksi | Average value: 16.3 GPa Grade Count:32 |
| Flexural Yield Strength | 75.0 - 250 MPa | 10900 - 36300 psi | Average value: 141 MPa Grade Count:64 |
| Flexural Modulus | 8.60 - 21.0 GPa | 1250 - 3050 ksi | Average value: 15.1 GPa Grade Count:52 |
| Compressive Yield Strength | 110 - 380 MPa | 16000 - 55100 psi | Average value: 237 MPa Grade Count:63 |
| Izod Impact, Notched | 0.209 - 1.84 J/cm | 0.392 - 3.44 ft-lb/in | Average value: 0.512 J/cm Grade Count:37 |
| Izod Impact, Notched (ISO) | 3.00 - 4.50 kJ/m2 | 1.43 - 2.14 ft-lb/in2 | Average value: 3.83 kJ/m2 Grade Count:3 |
| Charpy Impact Unnotched | 0.570 - 2.50 J/cm2 | 2.71 - 11.9 ft-lb/in2 | Average value: 1.20 J/cm2 Grade Count:18 |
| Charpy Impact, Notched | 0.191 - 0.620 J/cm2 | 0.909 - 2.95 ft-lb/in2 | Average value: 0.350 J/cm2 Grade Count:26 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.20e+11 - 8.10e+14 ohm-cm | 1.20e+11 - 8.10e+14 ohm-cm | Average value: 6.48e+13 ohm-cm Grade Count:27 |
| Surface Resistance | 1.00e+11 - 4.30e+13 ohm | 1.00e+11 - 4.30e+13 ohm | Average value: 1.61e+13 ohm Grade Count:10 |
| Insulation Resistance | 2.00e+7 - 1.00e+14 ohm | 2.00e+7 - 1.00e+14 ohm | Average value: 9.30e+12 ohm Grade Count:8 |
| Dielectric Constant | 4.30 - 6.70 | 4.30 - 6.70 | Average value: 5.03 Grade Count:18 |
| Dielectric Strength | 7.90 - 36.0 kV/mm | 201 - 914 kV/in | Average value: 16.0 kV/mm Grade Count:55 |
| Dielectric Breakdown | >= 20000 V @Temperature 90.0 - 90.0 °C | >= 20000 V @Temperature 194 - 194 °F | Average value: 16000 V Grade Count:1 |
| >= 15000 V @Temperature 90.0 - 90.0 °C | >= 15000 V @Temperature 194 - 194 °F | Average value: 16000 V Grade Count:1 | |
| >= 15000 V @Time 20.0 - 60.0 sec | >= 15000 V @Time 0.00556 - 0.0167 hour | Average value: 16000 V Grade Count:1 | |
| Dissipation Factor | 0.0100 - 0.0600 | 0.0100 - 0.0600 | Average value: 0.0289 Grade Count:17 |
| Arc Resistance | 50.0 - 193 sec | 50.0 - 193 sec | Average value: 166 sec Grade Count:29 |
| Comparative Tracking Index | 100 - 399 V | 100 - 399 V | Average value: 176 V Grade Count:29 |
| Hot Wire Ignition, HWI | 0.000 - 120 sec | 0.000 - 120 sec | Average value: 60.0 sec Grade Count:5 |
| High Amp Arc Ignition, HAI | 15.0 - 120 arcs | 15.0 - 120 arcs | Average value: 61.2 arcs Grade Count:5 |
| High Voltage Arc-Tracking Rate, HVTR | 0.000 - 10.0 mm/min | 0.000 - 0.394 in/min | Average value: 5.00 mm/min Grade Count:5 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 12.0 - 38.0 μm/m-°C | 6.67 - 21.1 μin/in-°F | Average value: 21.1 μm/m-°C Grade Count:36 |
| 35.0 - 48.0 μm/m-°C @Temperature 40.0 - 130 °C | 19.4 - 26.7 μin/in-°F @Temperature 104 - 266 °F | Average value: 41.7 μm/m-°C Grade Count:3 | |
| CTE, linear, Transverse to Flow | 26.8 - 55.0 μm/m-°C | 14.9 - 30.6 μin/in-°F | Average value: 39.8 μm/m-°C Grade Count:22 |
| Thermal Conductivity | 0.360 - 1.22 W/m-K | 2.50 - 8.47 BTU-in/hr-ft2-°F | Average value: 0.644 W/m-K Grade Count:14 |
| 0.500 - 0.580 W/m-K @Temperature 100 - 100 °C | 3.47 - 4.03 BTU-in/hr-ft2-°F @Temperature 212 - 212 °F | Average value: 0.540 W/m-K Grade Count:3 | |
| Maximum Service Temperature, Air | 150 - 225 °C | 302 - 437 °F | Average value: 165 °C Grade Count:25 |
| Deflection Temperature at 1.8 MPa (264 psi) | 164 - 315 °C | 327 - 599 °F | Average value: 238 °C Grade Count:61 |
| Deflection Temperature at 8.0 MPa | 150 - 171 °C | 302 - 340 °F | Average value: 166 °C Grade Count:3 |
| UL RTI, Electrical | 150 °C | 302 °F | Average value: 150 °C Grade Count:6 |
| UL RTI, Mechanical with Impact | 150 °C | 302 °F | Average value: 150 °C Grade Count:5 |
| UL RTI, Mechanical without Impact | 150 °C | 302 °F | Average value: 150 °C Grade Count:5 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:41 |
| Oxygen Index | 31.0 - 46.0 % | 31.0 - 46.0 % | Average value: 40.5 % Grade Count:4 |
| Shrinkage | 0.0100 - 0.300 % | 0.0100 - 0.300 % | Average value: 0.0882 % Grade Count:21 |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 155 - 180 °C | 311 - 356 °F | Average value: 168 °C Grade Count:15 |