| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Thickness | 76.2 microns | 3.00 mil | Polyethylene, Interleave | ||
| 457 microns | 18.0 mil | Prime Coated 162 Fiberglass, Substrate | |||
| 432 - 559 microns | 17.0 - 22.0 mil | Side 2 | |||
| 432 - 559 microns | 17.0 - 22.0 mil | Side 1 | |||
| 1450 - 1700 microns | 57.0 - 67.0 mil | Overall | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 40 - 50 | 40 - 50 | Compound Property | ||
| Tensile Strength | 5.58 - 6.83 MPa | 810 - 990 psi | Compound Property | ||
| Elongation at Break | 450 - 550 % | 450 - 550 % | Compound Property | ||
| Peel Strength | >= 1.05 kN/m | >= 6.00 pli | Bond Strength | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | >= 15.7 kV/mm | >= 400 kV/in | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Flammability Test | <= 3.0 | <= 3.0 | [in], Char Length; FTMS 191A; Method 5903 | ||
| <= 25 | <= 25 | [sec], Flame & Glow Time; FTMS 191A; Method 5903 | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Postcure Cycle | ||
| 15.0 min @Pressure 0.345 MPa, Temperature 177 °C | 0.250 hour @Pressure 50.0 psi, Temperature 350 °F | Recommended Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 21.1 °C | 6.00 Month @Temperature 70.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Red | ||||
| Total Product Weight (oz/yd2) | 58.2 - 68.2 | ||||
| Uncoated Fabric Break Strength | 420 lb/in | Fill Direction, Substrate Property | |||
| 700 lb/in | Warp Direction, Substrate Property | ||||