- 密度 [g/cm3]: 1.2
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in3 | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 76.2 microns | 3.00 mil | Interleave 1 | ||
| 76.2 microns | 3.00 mil | Interleave 2 | |||
| 127 microns | 5.00 mil | Side 1; Arlon SQA-TMS-003 | |||
| 127 microns | 5.00 mil | Substrate; Arlon SQA-TMS-003 | |||
| 254 microns | 10.0 mil | Side 2; Arlon SQA-TMS-003 | |||
| 508 microns | 20.0 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 47 | 47 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 6.89 MPa | 1000 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 400 % | 400 % | Silicone Property; ASTM D412 | ||
| Peel Strength | 2.63 kN/m | 15.0 pli | Bond Strength; Arlon SQA-TMS-011 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 37.4 kV/mm | 950 kV/in | Arlon SQA-TMS-020 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Flammability Test | <= 6.0 | <= 6.0 | [in], Char Length; FAR 25.853 App. F, Pt1, Sec A1ii | ||
| <= 15 | <= 15 | [sec], Flame Time; FAR 25.853 App. F, Pt1, Sec A1ii | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 121 °C | 0.250 hour @Pressure 50.0 psi, Temperature 250 °F | Recommended Bond Cycle | ||
| Shelf Life | 6.00 Month @Temperature 23.9 °C | 6.00 Month @Temperature 75.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Blue | Interleave 1 | |||
| Blue | Interleave 2 | ||||
| Red | |||||
| Red | Substrate | ||||
| Total Product Weight (oz/yd2) | 19.2 | Arlon SQA-TMS-025 | |||