- 密度 [g/cm3]: 1.25
- 拉伸強度 [MPa]: 94.0
- 斷裂伸長率 [%]: 148
- 彎曲模量 [MPa]: 3.90
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in3 | |
| Outgassing - Total Mass Loss | 0.070 % | 0.070 % | Average; ASTM E595 |
| Collected Volatile Condensable Material | 0.00 % | 0.00 % | ASTM E595 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 94.0 MPa @Temperature 23.0 °C | 13600 psi @Temperature 73.4 °F | |
| Elongation at Yield | 2.52 % | 2.52 % | Room Temperature |
| Tensile Modulus | 3.70 GPa @Temperature 23.0 °C | 537 ksi @Temperature 73.4 °F | |
| Flexural Yield Strength | 148 MPa | 21500 psi | Room Temperature |
| Flexural Modulus | 3.90 GPa | 566 ksi | Room Temperature |
| Compressive Yield Strength | 180 MPa | 26100 psi | Room Temperature |