- 拉伸強度 [MPa]: 710.0
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 710 MPa @Temperature -55.0 °C | 103000 psi @Temperature -67.0 °F | 90°, Dry |
| 765 MPa @Temperature -55.0 °C | 111000 psi @Temperature -67.0 °F | 0°, Dry | |
| 765 MPa @Temperature 93.3 °C | 111000 psi @Temperature 200 °F | 90°, Dry | |
| 793 MPa @Temperature 25.0 °C | 115000 psi @Temperature 77.0 °F | 90°, Dry | |
| 800 MPa @Temperature 90.6 °C | 116000 psi @Temperature 195 °F | 0°, Dry | |
| 827 MPa @Temperature 25.0 °C | 120000 psi @Temperature 77.0 °F | 0°, Dry | |
| Tensile Modulus | 65.5 GPa @Temperature -67.0 °C | 9500 ksi @Temperature -88.6 °F | 0°, Dry |
| 65.5 GPa @Temperature 77.0 °C | 9500 ksi @Temperature 171 °F | 90°, Dry | |
| 66.2 GPa @Temperature 195 °C | 9600 ksi @Temperature 383 °F | 0°, Dry | |
| 66.2 GPa @Temperature -67.0 °C | 9600 ksi @Temperature -88.6 °F | 90°, Dry | |
| 67.6 GPa @Temperature 77.0 °C | 9800 ksi @Temperature 171 °F | 0°, Dry | |
| 67.6 GPa @Temperature 200 °C | 9800 ksi @Temperature 392 °F | 90°, Dry | |
| Compressive Yield Strength | 586 MPa @Temperature 90.6 °C | 85000 psi @Temperature 195 °F | 0°, Wet |
| 600 MPa @Temperature 90.6 °C | 87000 psi @Temperature 195 °F | 0°, Wet, Fill Compression | |
| 696 MPa @Temperature 71.1 °C | 101000 psi @Temperature 160 °F | 0°, Wet, Fill Compression | |
| 703 MPa @Temperature 71.1 °C | 102000 psi @Temperature 160 °F | 0°, Wet | |
| 758 MPa @Temperature 90.6 °C | 110000 psi @Temperature 195 °F | 0°, Dry | |
| 786 MPa @Temperature 90.6 °C | 114000 psi @Temperature 195 °F | 0°, Dry, Fill Compression | |
| 800 MPa @Temperature 25.0 °C | 116000 psi @Temperature 77.0 °F | 0°, Wet, Fill Compression | |
| 876 MPa @Temperature -55.0 °C | 127000 psi @Temperature -67.0 °F | 0°, Dry, Fill Compression | |
| 876 MPa @Temperature 25.0 °C | 127000 psi @Temperature 77.0 °F | 0°, Dry, Fill Compression | |
| 883 MPa @Temperature 25.0 °C | 128000 psi @Temperature 77.0 °F | 0°, Dry | |
| 958 MPa @Temperature -55.0 °C | 139000 psi @Temperature -67.0 °F | 0°, Dry | |
| Compressive Modulus | 59.3 GPa @Temperature 71.1 °C | 8600 ksi @Temperature 160 °F | 0°, Wet |
| 60.0 GPa @Temperature -55.0 °C | 8700 ksi @Temperature -67.0 °F | 0°, Dry | |
| 60.0 GPa @Temperature 25.0 °C | 8700 ksi @Temperature 77.0 °F | 0°, Dry | |
| 60.7 GPa @Temperature 90.6 °C | 8800 ksi @Temperature 195 °F | 0°, Dry | |
| Shear Strength | 58.6 MPa @Temperature 90.6 °C | 8500 psi @Temperature 195 °F | 0° Short Beam, Wet |
| 58.6 MPa @Temperature 90.6 °C | 8500 psi @Temperature 195 °F | Fill Short Beam, Wet | |
| 70.3 MPa @Temperature 90.6 °C | 10200 psi @Temperature 195 °F | 0° Short Beam, Dry | |
| 70.3 MPa @Temperature 90.6 °C | 10200 psi @Temperature 195 °F | Fill Short Beam, Dry | |
| 71.7 MPa @Temperature 71.1 °C | 10400 psi @Temperature 160 °F | 0° Short Beam, Wet | |
| 74.5 MPa @Temperature -55.0 °C | 10800 psi @Temperature -67.0 °F | Fill Short Beam, Dry | |
| 75.2 MPa @Temperature 25.0 °C | 10900 psi @Temperature 77.0 °F | 0° Short Beam, Wet | |
| 78.6 MPa @Temperature 25.0 °C | 11400 psi @Temperature 77.0 °F | Fill Short Beam, Wet | |
| 81.4 MPa @Temperature 25.0 °C | 11800 psi @Temperature 77.0 °F | Fill Short Beam, Dry | |
| 84.1 MPa @Temperature 25.0 °C | 12200 psi @Temperature 77.0 °F | 0° Short Beam, Dry | |
| 101 MPa @Temperature -55.0 °C | 14600 psi @Temperature -67.0 °F | 0° Short Beam, Dry | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 121 °C | 250 °F | Epoxy Matrix Limit |