- 拉伸強度 [MPa]: 91.7
- 斷裂伸長率 [%]: 1860
- 彎曲模量 [MPa]: 15.2
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 91.7 MPa @Temperature 104 °C | 13300 psi @Temperature 220 °F | 90°, Dry |
| 111 MPa @Temperature 25.0 °C | 16100 psi @Temperature 77.0 °F | 90°, Dry | |
| 174 MPa @Temperature -55.0 °C | 25300 psi @Temperature -67.0 °F | 90°, Dry | |
| 428 MPa @Temperature 25.0 °C | 62100 psi @Temperature 77.0 °F | Open Hole Tensile, Dry | |
| 2540 MPa @Temperature 104 °C | 368000 psi @Temperature 220 °F | 0°, Dry | |
| 2570 MPa @Temperature -55.0 °C | 373000 psi @Temperature -67.0 °F | 0°, Dry | |
| 2720 MPa @Temperature 25.0 °C | 395000 psi @Temperature 77.0 °F | 0°, Dry | |
| Tensile Modulus | 10.3 GPa @Temperature 220 °C | 1500 ksi @Temperature 428 °F | 90°, Dry |
| 11.7 GPa @Temperature 77.0 °C | 1700 ksi @Temperature 171 °F | 90°, Dry | |
| 19.3 GPa @Temperature -67.0 °C | 2800 ksi @Temperature -88.6 °F | 90°, Dry | |
| 163 GPa @Temperature -67.0 °C | 23700 ksi @Temperature -88.6 °F | 0°, Dry | |
| 163 GPa @Temperature 220 °C | 23700 ksi @Temperature 428 °F | 0°, Dry | |
| 164 GPa @Temperature 77.0 °C | 23800 ksi @Temperature 171 °F | 0°, Dry | |
| Flexural Yield Strength | 1860 MPa @Temperature 25.0 °C | 270000 psi @Temperature 77.0 °F | 0°, Dry |
| Flexural Modulus | 15.2 GPa @Temperature 25.0 °C | 2200 ksi @Temperature 77.0 °F | 0°, Dry |
| Compressive Yield Strength | 170 MPa @Temperature 82.2 °C | 24600 psi @Temperature 180 °F | 0°, Wet, Fill Compression |
| 214 MPa @Temperature 25.0 °C | 31000 psi @Temperature 77.0 °F | Compression After Impact, Dry | |
| 226 MPa @Temperature 104 °C | 32800 psi @Temperature 220 °F | 0°, Dry, Fill Compression | |
| 234 MPa @Temperature 25.0 °C | 34000 psi @Temperature 77.0 °F | After 1500 in-in-lb/in impact, Dry | |
| 236 MPa @Temperature 25.0 °C | 34200 psi @Temperature 77.0 °F | 0°, Wet, Fill Compression | |
| 305 MPa @Temperature 25.0 °C | 44200 psi @Temperature 77.0 °F | 0°, Dry, Fill Compression | |
| 336 MPa @Temperature 25.6 °C | 48800 psi @Temperature 78.0 °F | Open Hole Compression, Dry | |
| 1480 MPa @Temperature 90.6 °C | 215000 psi @Temperature 195 °F | 0°, Dry | |
| 1690 MPa @Temperature 25.0 °C | 245000 psi @Temperature 77.0 °F | 0°, Dry | |
| Compressive Modulus | 150 GPa @Temperature 25.0 °C | 21700 ksi @Temperature 77.0 °F | 0°, Dry |
| 162 GPa @Temperature 90.6 °C | 23500 ksi @Temperature 195 °F | 0°, Dry | |
| Shear Strength | 80.0 MPa @Temperature 82.2 °C | 11600 psi @Temperature 180 °F | 0° Short Beam, Wet |
| 93.8 MPa @Temperature 104 °C | 13600 psi @Temperature 220 °F | 0° Short Beam, Dry | |
| 106 MPa @Temperature 104 °C | 15400 psi @Temperature 220 °F | +/- 45° In-Plane, Dry | |
| 115 MPa @Temperature 25.0 °C | 16700 psi @Temperature 77.0 °F | 0° Short Beam, Wet | |
| 120 MPa @Temperature 25.0 °C | 17400 psi @Temperature 77.0 °F | +/- 45° In-Plane, Dry | |
| 137 MPa @Temperature 25.0 °C | 19900 psi @Temperature 77.0 °F | 0° Short Beam, Dry | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 121 °C | 250 °F | Epoxy Matrix Limit |