- 拉伸強度 [MPa]: 75.2
- 斷裂伸長率 [%]: 1890
- 彎曲模量 [MPa]: 127
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 75.2 MPa @Temperature 93.3 °C | 10900 psi @Temperature 200 °F | 90°, Dry |
| 80.7 MPa @Temperature 25.0 °C | 11700 psi @Temperature 77.0 °F | 90°, Dry | |
| 438 MPa @Temperature 25.0 °C | 63500 psi @Temperature 77.0 °F | Open Hole Tensile, Dry | |
| 738 MPa @Temperature 25.0 °C | 107000 psi @Temperature 77.0 °F | Quasi-Isotropic 25/50/25, Dry | |
| 1900 MPa @Temperature -55.0 °C | 276000 psi @Temperature -67.0 °F | 0°, Dry | |
| 2020 MPa @Temperature 90.6 °C | 293000 psi @Temperature 195 °F | 0°, Dry | |
| 2140 MPa @Temperature 25.0 °C | 310000 psi @Temperature 77.0 °F | 0°, Dry | |
| Tensile Modulus | 8.41 GPa @Temperature 200 °C | 1220 ksi @Temperature 392 °F | 90°, Dry |
| 9.58 GPa @Temperature 77.0 °C | 1390 ksi @Temperature 171 °F | 90°, Dry | |
| 132 GPa @Temperature 195 °C | 19100 ksi @Temperature 383 °F | 0°, Dry | |
| 134 GPa @Temperature -67.0 °C | 19400 ksi @Temperature -88.6 °F | 0°, Dry | |
| 135 GPa @Temperature 77.0 °C | 19600 ksi @Temperature 171 °F | 0°, Dry | |
| Flexural Yield Strength | 1890 MPa @Temperature 25.0 °C | 274000 psi @Temperature 77.0 °F | 0°, Dry |
| Flexural Modulus | 127 GPa @Temperature 25.0 °C | 18400 ksi @Temperature 77.0 °F | 0°, Dry |
| Compressive Yield Strength | 186 MPa @Temperature 25.0 °C | 27000 psi @Temperature 77.0 °F | After 2500 in-in-lb/in impact, Dry |
| 193 MPa @Temperature 25.0 °C | 28000 psi @Temperature 77.0 °F | After 2000 in-in-lb/in impact, Dry | |
| 221 MPa @Temperature 25.0 °C | 32000 psi @Temperature 77.0 °F | After 1500 in-in-lb/in impact, Dry | |
| 239 MPa @Temperature 25.0 °C | 34600 psi @Temperature 77.0 °F | Compression After Impact, Dry | |
| 345 MPa @Temperature 25.0 °C | 50000 psi @Temperature 77.0 °F | After 500 in-in-lb/in impact, Dry | |
| 629 MPa @Temperature 25.0 °C | 91200 psi @Temperature 77.0 °F | Compression Before Impact, Dry | |
| 1270 MPa @Temperature 90.6 °C | 184000 psi @Temperature 195 °F | 0°, Dry | |
| 1270 MPa @Temperature 90.6 °C | 184000 psi @Temperature 195 °F | 0°, Wet | |
| 1400 MPa @Temperature 71.1 °C | 203000 psi @Temperature 160 °F | 0°, Wet | |
| 1530 MPa @Temperature 25.0 °C | 222000 psi @Temperature 77.0 °F | 0°, Dry | |
| 1590 MPa @Temperature -55.0 °C | 230000 psi @Temperature -67.0 °F | 0°, Dry | |
| Compressive Modulus | 117 GPa @Temperature 71.1 °C | 17000 ksi @Temperature 160 °F | 0°, Wet |
| 122 GPa @Temperature 90.6 °C | 17700 ksi @Temperature 195 °F | 0°, Dry | |
| 124 GPa @Temperature -55.0 °C | 18000 ksi @Temperature -67.0 °F | 0°, Dry | |
| 125 GPa @Temperature 90.6 °C | 18100 ksi @Temperature 195 °F | 0°, Wet | |
| 128 GPa @Temperature 25.0 °C | 18600 ksi @Temperature 77.0 °F | 0°, Dry | |
| Shear Strength | 77.9 MPa @Temperature 90.6 °C | 11300 psi @Temperature 195 °F | 0° Short Beam, Wet |
| 84.1 MPa @Temperature 71.1 °C | 12200 psi @Temperature 160 °F | 0° Short Beam, Wet | |
| 101 MPa @Temperature 90.6 °C | 14700 psi @Temperature 195 °F | 0° Short Beam, Dry | |
| 105 MPa @Temperature 93.3 °C | 15200 psi @Temperature 200 °F | +/- 45° In-Plane, Dry | |
| 114 MPa @Temperature 25.0 °C | 16600 psi @Temperature 77.0 °F | +/- 45° In-Plane, Dry | |
| 117 MPa @Temperature 25.0 °C | 16900 psi @Temperature 77.0 °F | 0° Short Beam, Wet | |
| 128 MPa @Temperature 25.0 °C | 18500 psi @Temperature 77.0 °F | 0° Short Beam, Dry | |
| 164 MPa @Temperature -55.0 °C | 23800 psi @Temperature -67.0 °F | 0° Short Beam, Dry | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 121 °C | 250 °F | Epoxy Matrix Limit |