- 密度 [g/cm3]: 1.19
- 拉伸強度 [MPa]: 56.0
- 斷裂伸長率 [%]: 88.0
- 彎曲模量 [MPa]: 3.20
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in3 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 56.0 MPa @Temperature 23.0 °C | 8120 psi @Temperature 73.4 °F | |
| Elongation at Break | 1.9 % | 1.9 % | |
| Tensile Modulus | 3.30 GPa @Temperature 23.0 °C | 479 ksi @Temperature 73.4 °F | |
| Flexural Yield Strength | 88.0 MPa | 12800 psi | Room Temperature |
| Flexural Modulus | 3.20 GPa | 464 ksi | Room Temperature |
| Thermal Properties | Metric | English | Comments |
| Glass Transition Temp, Tg | 197 °C | 387 °F | |