- 密度 [g/cm3]: 1.16
- 拉伸強度 [MPa]: 56.9
- 彎曲模量 [MPa]: 2.40
- 熱變形溫度 [℃]: 65.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.16 g/cc @Temperature 25.0 °C | 0.0419 lb/in3 @Temperature 77.0 °F | |||
| Viscosity | 300 cP @Temperature 30.0 °C | 300 cP @Temperature 86.0 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 56.9 - 57.1 MPa | 8250 - 8280 psi | ASTM D638M | ||
| Elongation at Break | 8.0 - 12 % | 8.0 - 12 % | ASTM D638M | ||
| Tensile Modulus | 2.54 - 2.62 GPa | 368 - 380 ksi | ASTM D638M | ||
| Flexural Strength | 83.8 - 86.7 MPa | 12200 - 12600 psi | ASTM D790M | ||
| Flexural Modulus | 2.40 - 2.45 GPa | 348 - 355 ksi | ASTM D790M | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 65.0 - 70.0 °C | 149 - 158 °F | ASTM D648-98c | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 53.0 - 54.0 °C | 127 - 129 °F | ASTM D648-98c | ||
| Descriptive Properties | |||||
| Appearance | Translucent | ||||
| Dp (mm) | 0.12 | Slope of cure-depth vs. ln(E) curve | |||
| E10 (mJ/cm2) | 57 | Exposure that gives 0.254mm thickness | |||
| Ec (mJ/cm2) | 6.38 | Critical exposure | |||