- 密度 [g/cm3]: 1.16
- 吸水率 [%]: 0.77
- 缺口沖擊強度: 0.14
- 拉伸強度 [MPa]: 51.7
- 彎曲模量 [MPa]: 2.36
- 熱變形溫度 [℃]: 55.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.16 g/cc @Temperature 25.0 °C | 0.0419 lb/in3 @Temperature 77.0 °F | |||
| Water Absorption | 0.77 % | 0.77 % | ASTM D570-98 | ||
| Viscosity | 300 cP @Temperature 30.0 °C | 300 cP @Temperature 86.0 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 84 - 85 | 84 - 85 | ASTM D2240 | ||
| Tensile Strength, Yield | 51.7 - 54.9 MPa | 7500 - 7960 psi | ASTM D638M | ||
| Elongation at Break | 6.0 - 12 % | 6.0 - 12 % | ASTM D638M | ||
| Tensile Modulus | 2.62 - 2.74 GPa | 380 - 397 ksi | ASTM D638M | ||
| Flexural Strength | 81.8 - 83.8 MPa | 11900 - 12200 psi | ASTM D790M | ||
| Flexural Modulus | 2.36 - 2.48 GPa | 342 - 360 ksi | ASTM D790M | ||
| Poissons Ratio | 0.43 - 0.45 | 0.43 - 0.45 | ASTM D638M | ||
| Izod Impact, Notched | 0.140 - 0.260 J/cm | 0.262 - 0.487 ft-lb/in | ASTM D256A | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 3.1 - 3.2 @Frequency 1.00e+6 Hz | 3.1 - 3.2 @Frequency 1.00e+6 Hz | ASTM D150-98 | ||
| 3.3 - 3.4 @Frequency 1000 Hz | 3.3 - 3.4 @Frequency 1000 Hz | ASTM D150-98 | |||
| 3.4 - 3.5 @Frequency 60.0 Hz | 3.4 - 3.5 @Frequency 60.0 Hz | ASTM D150-98 | |||
| Dielectric Strength | 14.4 - 15.3 kV/mm | 366 - 389 kV/in | ASTM D149-97a | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 65.1 - 68.1 μm/m-°C @Temperature -40.0 - 0.000 °C | 36.2 - 37.8 μin/in-°F @Temperature -40.0 - 32.0 °F | ASTM E831-00 | ||
| 84.7 - 95.3 μm/m-°C @Temperature 0.000 - 50.0 °C | 47.1 - 52.9 μin/in-°F @Temperature 32.0 - 122 °F | ASTM E831-00 | |||
| 93.8 - 116.9 μm/m-°C @Temperature 50.0 - 100 °C | 52.1 - 64.94 μin/in-°F @Temperature 122 - 212 °F | ASTM E831-00 | |||
| 147 - 155.4 μm/m-°C @Temperature 100 - 150 °C | 81.7 - 86.33 μin/in-°F @Temperature 212 - 302 °F | ASTM E831-00 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 55.0 - 58.0 °C | 131 - 136 °F | ASTM D648-98c | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 48.0 - 50.0 °C | 118 - 122 °F | ASTM D648-98c | ||
| Glass Transition Temp, Tg | 71.0 - 86.0 °C | 160 - 187 °F | ASTM E1545-00 | ||
| Descriptive Properties | |||||
| Appearance | Translucent | ||||
| Dp (mm) | 0.12 | Slope of cure-depth vs. ln(E) curve | |||
| E10 (mJ/cm2) | 57 | Exposure that gives 0.254mm thickness | |||
| Ec (mJ/cm2) | 6.38 | Critical exposure | |||