- 密度 [g/cm3]: 1.31
- 彎曲強度 [MPa]: 35.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 - 1.37 g/cc | 0.0473 - 0.0495 lb/in3 | |
| Solids Content | >= 99 % | >= 99 % | |
| Viscosity | 650000 cP @Shear Rate 1.00 1/s, Temperature 40.0 °C | 650000 cP @Shear Rate 1.00 1/s, Temperature 104 °F | cone/plate |
| 4.00e+6 cP @Shear Rate 1.00 1/s, Temperature 23.0 °C | 4.00e+6 cP @Shear Rate 1.00 1/s, Temperature 73.4 °F | cone/plate | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 35.0 MPa | 5080 psi | ISO 527-1 |
| Elongation at Break | 2.3 % | 2.3 % | ISO 527-1 |
| Modulus of Elasticity | 2.90 GPa | 421 ksi | ISO 527-1 |
| Adhesive Bond Strength | 16.9 MPa @Thickness 0.750 mm | 2450 psi @Thickness 0.0295 in | Lap Shear (25 x 10 x 0.2 mm) (CRS St 1203); EN 1465 |
| 23.7 MPa @Thickness 1.50 mm | 3440 psi @Thickness 0.0591 in | Lap Shear (25 x 10 x 0.2 mm) (CRS St 1203); EN 1465 | |
| Peel Strength | 3.70 kN/m | 21.1 pli | T-Peel (CRS St 1203, 0.5mm) |
| 8.00 kN/m | 45.6 pli | Impact Peel | |
| Thermal Properties | Metric | English | Comments |
| Flash Point | >= 150 °C | >= 302 °F | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 30.0 min | 0.500 hour | 180°C |