- 密度 [g/cm3]: 1.13
- 缺口沖擊強度: 0.252
- 拉伸強度 [MPa]: 44.0
- 彎曲模量 [MPa]: 2.57
- 熱變形溫度 [℃]: 65.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc @Temperature 25.0 °C | 0.0408 lb/in3 @Temperature 77.0 °F | |||
| Viscosity | 700 cP @Temperature 30.0 °C | 700 cP @Temperature 86.0 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 88 | 88 | ASTM D2240 | ||
| Tensile Strength, Yield | 44.0 MPa | 6380 psi | ASTM D638M | ||
| Elongation at Break | 1.3 - 7.5 % | 1.3 - 7.5 % | ASTM D638M | ||
| Modulus of Elasticity | 2.222 GPa | 322.3 ksi | ASTM D638M | ||
| Flexural Strength | 89.0 MPa | 12900 psi | ASTM D790M | ||
| Flexural Modulus | 2.57 GPa | 373 ksi | ASTM D790M | ||
| Izod Impact, Notched | 0.252 J/cm | 0.472 ft-lb/in | ASTM D256A | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | <= 65.0 °C | <= 149 °F | ASTM D648 | ||
| Descriptive Properties | |||||
| Appearance | Transparent Amber | ||||
| Dp (mm) | 0.123 | Slope of cure-depth vs. ln(E) curve | |||
| E10 (mJ/cm2) | 64 | Exposure that gives 0.254mm thickness | |||
| E5 (mJ/cm2) | 23 | Exposure that gives 0.127mm thickness | |||
| Ec (mJ/cm2) | 8 | Critical exposure | |||