- 密度 [g/cm3]: 1.13
- 缺口沖擊強度: 0.342
- 拉伸強度 [MPa]: 69.0
- 彎曲模量 [MPa]: 2.668
- 熱變形溫度 [℃]: 77.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc @Temperature 25.0 °C | 0.0408 lb/in3 @Temperature 77.0 °F | |||
| Viscosity | 700 cP @Temperature 30.0 °C | 700 cP @Temperature 86.0 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 85 | 85 | ASTM D2240 | ||
| Tensile Strength, Yield | 69.0 MPa | 10000 psi | ASTM D638M | ||
| Elongation at Break | 4.2 - 4.9 % | 4.2 - 4.9 % | ASTM D638M | ||
| Modulus of Elasticity | 2.413 GPa | 350.0 ksi | ASTM D638M | ||
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790M | ||
| Flexural Modulus | 2.668 GPa | 387.0 ksi | ASTM D790M | ||
| Izod Impact, Notched | 0.342 J/cm | 0.641 ft-lb/in | ASTM D256A | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 77.0 - 89.0 °C | 171 - 192 °F | ASTM D648 | ||
| Descriptive Properties | |||||
| Appearance | Transparent Amber | ||||
| Dp (mm) | 0.14 | Slope of cure-depth vs. ln(E) curve | |||
| E10 (mJ/cm2) | 51 | Exposure that gives 0.254mm thickness | |||
| E5 (mJ/cm2) | 20 | Exposure that gives 0.127mm thickness | |||
| Ec (mJ/cm2) | 8.2 | Critical exposure | |||