- 密度 [g/cm3]: 1.16
- 吸水率 [%]: 0.61
- 缺口沖擊強度: 0.09
- 拉伸強度 [MPa]: 66.1
- 彎曲模量 [MPa]: 2.28
- 熱變形溫度 [℃]: 93.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.16 g/cc @Temperature 25.0 °C | 0.0419 lb/in3 @Temperature 77.0 °F | |||
| Water Absorption | 0.61 % | 0.61 % | ASTM D570-98 | ||
| Viscosity | 350 cP @Temperature 30.0 °C | 350 cP @Temperature 86.0 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 86 - 87 | 86 - 87 | ASTM D2240 | ||
| Tensile Strength, Yield | 66.1 - 68.1 MPa | 9590 - 9880 psi | ASTM D638M | ||
| Elongation at Break | 6.0 - 9.0 % | 6.0 - 9.0 % | ASTM D638M | ||
| Tensile Modulus | 2.88 - 2.96 GPa | 418 - 429 ksi | ASTM D638M | ||
| Flexural Strength | 84.9 - 87.7 MPa | 12300 - 12700 psi | ASTM D790M | ||
| Flexural Modulus | 2.28 - 2.34 GPa | 331 - 339 ksi | ASTM D790M | ||
| Poissons Ratio | 0.40 - 0.42 | 0.40 - 0.42 | ASTM D638M | ||
| Izod Impact, Notched | 0.0900 - 0.210 J/cm | 0.169 - 0.393 ft-lb/in | ASTM D256A | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 2.9 - 3.0 @Frequency 1.00e+6 Hz | 2.9 - 3.0 @Frequency 1.00e+6 Hz | ASTM D150-98 | ||
| 3.1 - 3.2 @Frequency 1000 Hz | 3.1 - 3.2 @Frequency 1000 Hz | ASTM D150-98 | |||
| 3.1 - 3.3 @Frequency 60.0 Hz | 3.1 - 3.3 @Frequency 60.0 Hz | ASTM D150-98 | |||
| Dielectric Strength | 13.8 - 14.1 kV/mm | 351 - 358 kV/in | ASTM D149-97a | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 67.3 - 68.2 μm/m-°C @Temperature -40.0 - 0.000 °C | 37.4 - 37.9 μin/in-°F @Temperature -40.0 - 32.0 °F | ASTM E831-00 | ||
| 82.2 - 86.4 μm/m-°C @Temperature 0.000 - 50.0 °C | 45.7 - 48.0 μin/in-°F @Temperature 32.0 - 122 °F | ASTM E831-00 | |||
| 110.4 - 116 μm/m-°C @Temperature 50.0 - 100 °C | 61.33 - 64.4 μin/in-°F @Temperature 122 - 212 °F | ASTM E831-00 | |||
| 152.7 - 163.2 μm/m-°C @Temperature 100 - 150 °C | 84.83 - 90.67 μin/in-°F @Temperature 212 - 302 °F | ASTM E831-00 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 - 98.0 °C | 199 - 208 °F | ASTM D648-98c | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 - 78.0 °C | 165 - 172 °F | ASTM D648-98c | ||
| Glass Transition Temp, Tg | 78.0 - 96.0 °C | 172 - 205 °F | ASTM E1545-00 | ||
| Descriptive Properties | |||||
| Appearance | White | ||||
| Dp (mm) | 0.11 | Slope of cure-depth vs. ln(E) curve | |||
| E10 (mJ/cm2) | 67.6 | Exposure that gives 0.254mm thickness | |||
| Ec (mJ/cm2) | 6.73 | Critical exposure | |||