- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 0.93
- 缺口沖擊強度: 0.44
- 拉伸強度 [MPa]: 17.0
- 彎曲模量 [MPa]: 0.768
- 熱變形溫度 [℃]: 47.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc @Temperature 25.0 °C | 0.0408 lb/in3 @Temperature 77.0 °F | |||
| Water Absorption | 0.93 % | 0.93 % | ASTM D570-98 | ||
| Viscosity | 475 cP @Temperature 30.0 °C | 475 cP @Temperature 86.0 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 70 - 74 | 70 - 74 | ASTM D2240 | ||
| Tensile Strength, Yield | 17.0 - 20.0 MPa | 2470 - 2900 psi | ASTM D638M | ||
| Elongation at Break | 25 - 30 % | 25 - 30 % | ASTM D638M | ||
| Modulus of Elasticity | 0.553 - 0.850 GPa | 80.2 - 123 ksi | ASTM D638M | ||
| Flexural Strength | 24.0 - 30.0 MPa | 3480 - 4350 psi | ASTM D790M | ||
| Flexural Modulus | 0.768 - 0.900 GPa | 111 - 131 ksi | ASTM D790M | ||
| Poissons Ratio | 0.43 | 0.43 | ASTM D638M | ||
| Izod Impact, Notched | 0.440 - 0.480 J/cm | 0.824 - 0.899 ft-lb/in | ASTM D256A | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 3.94 @Frequency 1.00e+6 Hz | 3.94 @Frequency 1.00e+6 Hz | ASTM D150-98 | ||
| 4.66 @Frequency 1000 Hz | 4.66 @Frequency 1000 Hz | ASTM D150-98 | |||
| 5.33 @Frequency 60.0 Hz | 5.33 @Frequency 60.0 Hz | ASTM D150-98 | |||
| Dielectric Strength | 14.1 kV/mm | 358 kV/in | ASTM D149-97a | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 96.8 μm/m-°C @Temperature -40.0 - 0.000 °C | 53.8 μin/in-°F @Temperature -40.0 - 32.0 °F | ASTM E831-00 | ||
| 144 μm/m-°C @Temperature 100 - 150 °C | 80.0 μin/in-°F @Temperature 212 - 302 °F | ASTM E831-00 | |||
| 149.5 μm/m-°C @Temperature 0.000 - 50.0 °C | 83.06 μin/in-°F @Temperature 32.0 - 122 °F | ASTM E831-00 | |||
| 178.7 μm/m-°C @Temperature 50.0 - 100 °C | 99.28 μin/in-°F @Temperature 122 - 212 °F | ASTM E831-00 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 47.0 - 50.0 °C | 117 - 122 °F | ASTM D648-98c | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 36.0 - 38.0 °C | 96.8 - 100 °F | ASTM D648-98c | ||
| Glass Transition Temp, Tg | 57.0 - 60.0 °C | 135 - 140 °F | ASTM E1545-00 | ||
| Descriptive Properties | |||||
| Appearance | White | ||||
| Dp (mm) | 0.14 | Slope of cure-depth vs. ln(E) curve | |||
| E10 (mJ/cm2) | 95 | Exposure that gives 0.254mm thickness | |||
| Ec (mJ/cm2) | 15 | Critical exposure | |||