- 密度 [g/cm3]: 1.15
- 吸水率 [%]: 0.9
- 缺口沖擊強(qiáng)度: 2.7
- 彎曲模量 [MPa]: 11.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.15 - 1.25 g/cc | 0.0415 - 0.0452 lb/in3 | ASTM D792 | ||
| Water Absorption | 0.90 % @Temperature 50.0 °C, Time 173000 sec | 0.90 % @Temperature 122 °F, Time 48.0 hour | ASTM D570 | ||
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 48.0 MPa | 6960 psi | ASTM D638 | ||
| Flexural Strength | 103 MPa | 14900 psi | at rupture; ASTM D790 | ||
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D790 | ||
| Compressive Strength | 166 MPa | 24100 psi | ASTM D695 | ||
| Izod Impact, Notched | 2.70 J/cm | 5.06 ft-lb/in | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 2.8 @Frequency 1.00e+6 Hz | 2.8 @Frequency 1.00e+6 Hz | wet; ASTM D150 | ||
| Dielectric Strength | 9.80 kV/mm @Frequency 60.0 Hz | 249 kV/in @Frequency 60.0 Hz | step-by-step, wet; ASTM D149 | ||
| Dissipation Factor | 0.026 @Frequency 1.00e+6 Hz | 0.026 @Frequency 1.00e+6 Hz | wet; ASTM D150 | ||
| Arc Resistance | 120 sec | 120 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 280 °C | >= 536 °F | Post Baked; ASTM D648A | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Form | Coarse Flake | ||||
| Molding Method | Compression | ||||
| Transfer | |||||