- 密度 [g/cm3]: 0.86
- 吸水率 [%]: 0.03
- 拉伸強度 [MPa]: 1.03
- 斷裂伸長率 [%]: 92.0
- 彎曲強度 [MPa]: 5.17
- 彎曲模量 [MPa]: 0.00350
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.860 - 2.60 g/cc | 0.0311 - 0.0939 lb/in3 | Average value: 1.33 g/cc Grade Count:103 |
| 1.025 - 1.06 g/cc @Temperature 15.0 - 15.0 °C | 0.03703 - 0.0383 lb/in3 @Temperature 59.0 - 59.0 °F | Average value: 1.05 g/cc Grade Count:3 | |
| Solids Content | 59.0 - 100 % | 59.0 - 100 % | Average value: 78.2 % Grade Count:20 |
| Volatiles | 5.00e-7 - 3.92 % | 5.00e-7 - 3.92 % | Average value: 0.355 % Grade Count:34 |
| Water Absorption | 0.0300 - 1.00 % | 0.0300 - 1.00 % | Average value: 0.298 % Grade Count:25 |
| Moisture Absorption at Equilibrium | 2.80 - 9.40 % | 2.80 - 9.40 % | Average value: 5.16 % Grade Count:7 |
| Viscosity | 0.650 - 1.20e+6 cP | 0.650 - 1.20e+6 cP | Average value: 36500 cP Grade Count:102 |
| 15.0 - 78000 cP @Temperature 40.0 - 156 °C | 15.0 - 78000 cP @Temperature 104 - 313 °F | Average value: 8950 cP Grade Count:4 | |
| Molecular Weight | 158 - 1690 g/mol | 158 - 1690 g/mol | Average value: 661 g/mol Grade Count:11 |
| Linear Mold Shrinkage | 0.00100 - 0.00400 cm/cm | 0.00100 - 0.00400 in/in | Average value: 0.00240 cm/cm Grade Count:5 |
| Vapor Pressure | 2.10e-8 - 0.0100 bar | 0.0000158 - 7.50 torr | Average value: 0.00250 bar Grade Count:4 |
| 0.0100 - 0.0100 bar @Temperature 50.0 - 50.0 °C | 7.50 - 7.50 torr @Temperature 122 - 122 °F | Average value: 0.00400 bar Grade Count:3 | |
| Storage Temperature | 23.0 - 25.0 °C | 73.4 - 77.0 °F | Average value: 23.5 °C Grade Count:4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 50.0 - 95.0 | 50.0 - 95.0 | Average value: 80.4 Grade Count:27 |
| Tensile Strength, Ultimate | 5.17 - 97.0 MPa | 750 - 14100 psi | Average value: 33.7 MPa Grade Count:31 |
| 35.8527 - 35.8527 MPa @Temperature 149 - 149 °C | 5200.01 - 5200.01 psi @Temperature 300 - 300 °F | Average value: 35.9 MPa Grade Count:1 | |
| Tensile Strength, Yield | 1.03 - 2900 MPa | 150 - 420000 psi | Average value: 576 MPa Grade Count:102 |
| 4.137 - 2571.74 MPa @Temperature -55.0 - 190 °C | 600.0 - 373001 psi @Temperature -67.0 - 374 °F | Average value: 626 MPa Grade Count:17 | |
| Elongation at Break | 0.000 - 50.0 % | 0.000 - 50.0 % | Average value: 9.35 % Grade Count:33 |
| 2.40 - 6.90 % @Temperature 75.0 - 300 °C | 2.40 - 6.90 % @Temperature 167 - 572 °F | Average value: 4.65 % Grade Count:1 | |
| Elongation at Yield | 1.00 - 13.0 % | 1.00 - 13.0 % | Average value: 3.49 % Grade Count:30 |
| Modulus of Elasticity | 0.00370 - 215 GPa | 0.537 - 31200 ksi | Average value: 35.9 GPa Grade Count:99 |
| 1.572 - 164.095 GPa @Temperature -67.0 - 220 °C | 228.0 - 23800.4 ksi @Temperature -88.6 - 428 °F | Average value: 57.7 GPa Grade Count:17 | |
| Flexural Yield Strength | 92.0 - 1890 MPa | 13300 - 274000 psi | Average value: 921 MPa Grade Count:33 |
| 108.937 - 1380.95 MPa @Temperature 50.0 - 177 °C | 15800.0 - 200290 psi @Temperature 122 - 350 °F | Average value: 942 MPa Grade Count:7 | |
| Flexural Modulus | 0.00350 - 205 GPa | 0.508 - 29700 ksi | Average value: 56.0 GPa Grade Count:34 |
| 3.13711 - 109.075 GPa @Temperature 50.0 - 177 °C | 455.007 - 15820.2 ksi @Temperature 122 - 350 °F | Average value: 63.0 GPa Grade Count:7 | |
| Compressive Yield Strength | 2.76 - 1690 MPa | 400 - 246000 psi | Average value: 358 MPa Grade Count:79 |
| 52.0 - 1585.79 MPa @Temperature -55.0 - 177 °C | 7540 - 230000 psi @Temperature -67.0 - 351 °F | Average value: 574 MPa Grade Count:21 | |
| Compressive Modulus | 0.0552 - 168 GPa | 8.00 - 24300 ksi | Average value: 45.2 GPa Grade Count:59 |
| 12.0 - 162.027 GPa @Temperature -55.0 - 177 °C | 1740 - 23500.4 ksi @Temperature -67.0 - 351 °F | Average value: 62.1 GPa Grade Count:16 | |
| Poissons Ratio | 0.350 - 0.420 | 0.350 - 0.420 | Average value: 0.389 Grade Count:10 |
| Fracture Toughness | 0.433 - 3.69 MPa-m? | 0.394 - 3.36 ksi-in? | Average value: 1.33 MPa-m? Grade Count:18 |
| Shear Modulus | 1.07 - 5.86 GPa | 155 - 850 ksi | Average value: 3.20 GPa Grade Count:23 |
| 2.96475 - 35.0 GPa @Temperature 80.0 - 175 °C | 430.007 - 5080 ksi @Temperature 176 - 347 °F | Average value: 13.7 GPa Grade Count:2 | |
| Shear Strength | 6.76 - 137 MPa | 980 - 19900 psi | Average value: 78.6 MPa Grade Count:51 |
| 11.0 - 164.095 MPa @Temperature -55.0 - 177 °C | 1600 - 23800.0 psi @Temperature -67.0 - 351 °F | Average value: 58.8 MPa Grade Count:26 | |
| Adhesive Bond Strength | 5.86 - 24.1 MPa | 850 - 3500 psi | Average value: 12.8 MPa Grade Count:26 |
| Toughness | 51.0 - 541 J | 37.6 - 399 ft-lb | Average value: 220 J Grade Count:8 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 0.00100 - 8.10e+15 ohm-cm | 0.00100 - 8.10e+15 ohm-cm | Average value: 2.13e+15 ohm-cm Grade Count:31 |
| 1.80e+15 - 1.50e+16 ohm-cm @Temperature 75.0 - 300 °C | 1.80e+15 - 1.50e+16 ohm-cm @Temperature 167 - 572 °F | Average value: 8.40e+15 ohm-cm Grade Count:1 | |
| Dielectric Constant | 2.96 - 5.40 | 2.96 - 5.40 | Average value: 4.45 Grade Count:30 |
| 2.95 - 2.95 @Temperature 149 - 149 °C | 2.95 - 2.95 @Temperature 300 - 300 °F | Average value: 2.95 Grade Count:1 | |
| 2.95 - 2.95 @Frequency 60.0 - 60.0 Hz | 2.95 - 2.95 @Frequency 60.0 - 60.0 Hz | Average value: 2.95 Grade Count:1 | |
| Dielectric Strength | 14.4 - 17.3 kV/mm | 365 - 440 kV/in | Average value: 16.0 kV/mm Grade Count:28 |
| Dissipation Factor | 0.00300 - 0.00300 @Temperature 149 - 149 °C | 0.00300 - 0.00300 @Temperature 300 - 300 °F | Average value: 0.00300 Grade Count:1 |
| 0.00300 - 0.00300 @Frequency 60.0 - 60.0 Hz | 0.00300 - 0.00300 @Frequency 60.0 - 60.0 Hz | Average value: 0.00300 Grade Count:1 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 16.0 - 85.5 μm/m-°C | 8.89 - 47.5 μin/in-°F | Average value: 50.8 μm/m-°C Grade Count:37 |
| 98.0 - 180 μm/m-°C @Temperature >=27.0 °C | 54.4 - 100 μin/in-°F @Temperature >=80.6 °F | Average value: 131 μm/m-°C Grade Count:9 | |
| Thermal Conductivity | 0.140 - 1.28 W/m-K | 0.972 - 8.88 BTU-in/hr-ft2-°F | Average value: 0.541 W/m-K Grade Count:25 |
| Melting Point | -80.0 - 130 °C | -112 - 266 °F | Average value: 40.0 °C Grade Count:4 |
| Maximum Service Temperature, Air | 25.0 - 260 °C | 77.0 - 500 °F | Average value: 136 °C Grade Count:61 |
| Softening Point | 12.0 - 150 °C | 53.6 - 302 °F | Average value: 74.4 °C Grade Count:33 |
| Minimum Service Temperature, Air | -73.3 - -20.0 °C | -100 - -4.00 °F | Average value: -44.0 °C Grade Count:32 |
| Glass Transition Temp, Tg | 5.00 - 285 °C | 41.0 - 545 °F | Average value: 122 °C Grade Count:78 |
| Flash Point | 28.0 - 231 °C | 82.4 - 448 °F | Average value: 122 °C Grade Count:19 |
| Shrinkage | 0.250 - 1.60 % | 0.250 - 1.60 % | Average value: 1.17 % Grade Count:6 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.46 - 1.54 | 1.46 - 1.54 | Average value: 1.50 Grade Count:16 |
| Transmission, Visible | 90.0 % | 90.0 % | Average value: 90.0 % Grade Count:5 |
| Gardner Color Number | 0.200 - 6.00 | 0.200 - 6.00 | Average value: 0.885 Grade Count:33 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 25.0 - 170 °C | 77.0 - 338 °F | Average value: 109 °C Grade Count:13 |
| Moisture Content | 0.100 - 0.200 % | 0.100 - 0.200 % | Average value: 0.171 % Grade Count:7 |
| Cure Time | 480 - 4320 min | 8.00 - 72.0 hour | Average value: 2080 min Grade Count:12 |
| 10.02 - 720 min @Temperature 45.0 - 180 °C | 0.1670 - 12.0 hour @Temperature 113 - 356 °F | Average value: 121 min Grade Count:20 | |
| Pot Life | 8.00 - 720 min | 8.00 - 720 min | Average value: 92.7 min Grade Count:30 |
| Gel Time | 1.00 - 120 min @Temperature 60.0 - 240 °C | 1.00 - 120 min @Temperature 140 - 464 °F | Average value: 30.2 min Grade Count:17 |
| Shelf Life | 0.750 - 15.0 Month | 0.750 - 15.0 Month | Average value: 7.22 Month Grade Count:8 |
| 3.00 - 18.0 Month @Temperature -18.0 - 10.0 °C | 3.00 - 18.0 Month @Temperature -0.400 - 50.0 °F | Average value: 11.9 Month Grade Count:53 | |
| Component Elements Properties | Metric | English | Comments |
| H2O | 0.100 - 0.200 % | 0.100 - 0.200 % | Average value: 0.167 % Grade Count:3 |