- 密度 [g/cm3]: 1.92
- 吸水率 [%]: 0.2
- 缺口沖擊強度: 0.37
- 彎曲模量 [MPa]: 15.1
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.900 g/cc | 0.0325 lb/in3 | ASTM D1895 | ||
| Density | 1.92 g/cc | 0.0694 lb/in3 | ASTM D792 | ||
| Water Absorption | 0.20 % @Temperature 50.0 °C, Time 173000 sec | 0.20 % @Temperature 122 °F, Time 48.0 hour | ASTM D570 | ||
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | ASTM D638 | ||
| Flexural Strength | 130 MPa | 18900 psi | at rupture; ASTM D790 | ||
| Flexural Modulus | 15.1 GPa | 2190 ksi | ASTM D790 | ||
| Compressive Strength | 240 MPa | 34800 psi | ASTM D695 | ||
| Izod Impact, Notched | 0.370 J/cm | 0.693 ft-lb/in | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 4.1 @Frequency 1.00e+6 Hz | 4.1 @Frequency 1.00e+6 Hz | wet; ASTM D150 | ||
| Dielectric Strength | 12.9 kV/mm @Frequency 60.0 Hz | 328 kV/in @Frequency 60.0 Hz | step-by-step, wet; ASTM D149 | ||
| 14.3 kV/mm @Frequency 60.0 Hz | 363 kV/in @Frequency 60.0 Hz | short time, wet; ASTM D149 | |||
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | wet; ASTM D150 | ||
| Arc Resistance | 180 sec | 180 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 37.0 μm/m-°C | 20.6 μin/in-°F | ASTM E831 | ||
| Maximum Service Temperature, Air | 130 °C | 266 °F | UL Temperature Index; UL 746B | ||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 282 °C | >= 540 °F | Post Baked; ASTM D648A | ||
| Flammability, UL94 | V-0 @Thickness 6.40 mm | V-0 @Thickness 0.252 in | |||
| Descriptive Properties | |||||
| Colors | Black, Blue, Green, Gray | ||||
| Form | Granular | ||||
| Molding Method | Compression | ||||
| Injection | |||||
| Transfer | |||||