- 密度 [g/cm3]: 1.39
- 吸水率 [%]: 0.09
- 缺口沖擊強度: 12.0
- 拉伸強度 [MPa]: 120.0
- 彎曲模量 [MPa]: 10.4
- 熱變形溫度 [℃]: 255.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in3 | ISO 1183 B |
| Filler Content | 30 % | 30 % | Glass |
| Water Absorption | 0.090 % | 0.090 % | 24 hours |
| Linear Mold Shrinkage | 0.0015 - 0.0030 cm/cm @Thickness 2.00 mm | 0.0015 - 0.0030 in/in @Thickness 0.0787 in | ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Thickness 2.00 mm | 0.0070 - 0.0090 in/in @Thickness 0.0787 in | ISO 294 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 120 MPa | 17400 psi | ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 |
| Tensile Modulus | 9.00 GPa | 1310 ksi | ISO 527 |
| Flexural Strength | 190 MPa | 27600 psi | ISO 178 |
| Flexural Modulus | 10.4 GPa | 1510 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m2 @Temperature 23.0 °C | 5.71 ft-lb/in2 @Temperature 73.4 °F | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m2 | 23.8 ft-lb/in2 | ISO 180/1U |
| Charpy Impact Unnotched | 3.90 J/cm2 @Temperature 23.0 °C | 18.6 ft-lb/in2 @Temperature 73.4 °F | ISO 179 |
| Charpy Impact, Notched | 0.900 J/cm2 @Temperature 23.0 °C | 4.28 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.30e+18 ohm-cm | 1.30e+18 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.2 @Frequency 1e+6 Hz | 3.2 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 31.0 kV/mm @Thickness 0.800 mm | 787 kV/in @Thickness 0.0315 in | ASTM D149 |
| Dissipation Factor | 0.0020 @Frequency 1e+6 Hz | 0.0020 @Frequency 1e+6 Hz | ASTM D150 |
| Comparative Tracking Index | 425 V | 425 V | Solution A; IEC 112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 18.0 μm/m-°C @Temperature 100 °C | 10.0 μin/in-°F @Temperature 212 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | ISO 75B |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75-2 |
| Vicat Softening Point | 255 °C | 491 °F | A/10N; ISO 306 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | |
| Oxygen Index | 28 % | 28 % | ISO 4589-1984 |
| Glow Wire Test | 960 °C @Thickness 1.00 mm | 1760 °F @Thickness 0.0394 in | IEC 695-2-1 |
| 960 °C @Thickness 2.00 mm | 1760 °F @Thickness 0.0787 in | IEC 695-2-1 | |
| 960 °C @Thickness 3.00 mm | 1760 °F @Thickness 0.118 in | IEC 695-2-1 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 285 - 310 °C | 545 - 590 °F | pre-drying not required |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| 140 - 155 °C | 284 - 311 °F | for optimal gloss and heat resistance | |