- 密度 [g/cm3]: 1.67
- 缺口沖擊強度: 7.0
- 彎曲模量 [MPa]: 16.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.67 g/cc | 0.0603 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 96 | 96 | ISO 2039-2 | ||
| Tensile Strength at Break | 145 MPa | 21000 psi | 5mm/min; ISO 527-2/1A | ||
| Tensile Stress | 20.83 MPa @Strain 0.130 %, Temperature 23.0 °C | 3021 psi @Strain 0.130 %, Temperature 73.4 °F | |||
| 37.89 MPa @Strain 0.270 %, Temperature 23.0 °C | 5495 psi @Strain 0.270 %, Temperature 73.4 °F | ||||
| 55.06 MPa @Strain 0.410 %, Temperature 23.0 °C | 7986 psi @Strain 0.410 %, Temperature 73.4 °F | ||||
| 70.68 MPa @Strain 0.550 %, Temperature 23.0 °C | 10250 psi @Strain 0.550 %, Temperature 73.4 °F | ||||
| 85.36 MPa @Strain 0.690 %, Temperature 23.0 °C | 12380 psi @Strain 0.690 %, Temperature 73.4 °F | ||||
| 99.77 MPa @Strain 0.820 %, Temperature 23.0 °C | 14470 psi @Strain 0.820 %, Temperature 73.4 °F | ||||
| 113.19 MPa @Strain 0.960 %, Temperature 23.0 °C | 16417 psi @Strain 0.960 %, Temperature 73.4 °F | ||||
| 124.9 MPa @Strain 1.10 %, Temperature 23.0 °C | 18120 psi @Strain 1.10 %, Temperature 73.4 °F | ||||
| 135.82 MPa @Strain 1.24 %, Temperature 23.0 °C | 19699 psi @Strain 1.24 %, Temperature 73.4 °F | ||||
| 145.38 MPa @Strain 1.38 %, Temperature 23.0 °C | 21086 psi @Strain 1.38 %, Temperature 73.4 °F | ||||
| Elongation at Break | 1.0 % | 1.0 % | 5mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 16.0 GPa | 2320 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 230 MPa | 33400 psi | ISO 178 | ||
| Flexural Modulus | 16.0 GPa | 2320 ksi | ISO 178 | ||
| Compressive Strength | 134 MPa @Strain 1.00 % | 19400 psi @Strain 1.00 % | ISO 604 | ||
| Compressive Modulus | 16.0 GPa | 2320 ksi | ISO 604 | ||
| Izod Impact, Notched (ISO) | 7.00 kJ/m2 | 3.33 ft-lb/in2 | ISO 180/1A | ||
| Charpy Impact, Notched | 1.10 J/cm2 | 5.23 ft-lb/in2 | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 3.7 @Frequency 1.00e+6 Hz | 3.7 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 4.2 @Frequency 100 Hz | 4.2 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0050 @Frequency 1.00e+6 Hz | 0.0050 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 0.020 @Frequency 100 Hz | 0.020 @Frequency 100 Hz | IEC 60250 | |||
| Arc Resistance | 165 sec | 165 sec | |||
| Comparative Tracking Index | 175 V | 175 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 11.0 μm/m-°C | 6.11 μin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 21.0 μm/m-°C | 11.7 μin/in-°F | ISO 11359-2 | ||
| Melting Point | 280 °C | 536 °F | ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 270 °C | 518 °F | ISO 75-1, -2 | ||
| Flammability, UL94 | V-0 @Thickness 0.400 mm | V-0 @Thickness 0.0157 in | |||
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 30.0 °C | 68.0 - 86.0 °F | hopper | ||
| 80.0 - 120 °C | 176 - 248 °F | cavity | |||
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| Zone 1 | 295 - 305 °C | 563 - 581 °F | |||
| Zone 2 | 300 - 310 °C | 572 - 590 °F | |||
| Zone 3 | 300 - 310 °C | 572 - 590 °F | |||
| Zone 4 | 300 - 310 °C | 572 - 590 °F | |||
| Die Temperature | 300 - 310 °C | 572 - 590 °F | |||
| Melt Temperature | 293 °C | 559 °F | ISO 294 | ||
| 300 - 315 °C | 572 - 599 °F | ||||
| Mold Temperature | 100 °C | 212 °F | ISO 294 | ||
| Injection Velocity | 150 mm/sec | 5.91 in/sec | ISO 294 | ||
| Drying Temperature | 150 °C | 302 °F | |||
| Dry Time | 4 - 24.0 hour | 4 - 24.0 hour | |||
| Moisture Content | 0.010 % | 0.010 % | Necessary low maximum | ||
| Injection Pressure | 69.0 MPa | 10000 psi | ISO 294 | ||
| 50.0 - 150.0 MPa | 7250 - 21750 psi | ||||
| Hold Pressure | 50.0 - 150.0 MPa | 7250 - 21750 psi | |||
| Back Pressure | <= 3.00 MPa | <= 435 psi | |||
| Screw Speed | 80 rpm @Diameter 40.0 mm | 80 rpm @Diameter 1.57 in | |||
| 140 rpm @Diameter 25.0 mm | 140 rpm @Diameter 0.984 in | ||||
| 200 rpm @Diameter 16.0 mm | 200 rpm @Diameter 0.630 in | ||||
| Hot-Working Temperature | 300 - 310 °C | 572 - 590 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | very fast | ||||
| Remarks | When using short metering strokes an accumulator is recommended to get short injection times | ||||