- 密度 [g/cm3]: 1.74
- 彎曲模量 [MPa]: 17.8
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.74 g/cc | 0.0629 lb/in3 | ISO 1183 |
| Density of Compound | 1.45 g/cc | 0.0524 lb/in3 | melt; Internal |
| Linear Mold Shrinkage, Flow | 0.000500 cm/cm | 0.000500 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00500 cm/cm | 0.00500 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 58.0 | 58.0 | ISO 2039-2 |
| Tensile Strength at Break | 120 MPa | 17400 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 0.900 % | 0.900 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 18.0 GPa | 2610 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 180 MPa | 26100 psi | ISO 178 |
| Flexural Modulus | 17.8 GPa | 2580 ksi | ISO 178 |
| Charpy Impact Unnotched | 1.80 J/cm2 | 8.57 ft-lb/in2 | ISO 179/1eU |
| 1.30 J/cm2 @Temperature -30.0 °C | 6.19 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 1.00 J/cm2 | 4.76 ft-lb/in2 | ISO 179/1eA |
| 1.00 J/cm2 @Temperature -30.0 °C | 4.76 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 4.40 @Frequency 1.00e+6 Hz | 4.40 @Frequency 1.00e+6 Hz | IEC 60250 |
| 4.80 @Frequency 100 Hz | 4.80 @Frequency 100 Hz | IEC 60250 | |
| Dielectric Strength | 36.0 kV/mm | 914 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0130 @Frequency 100 Hz | 0.0130 @Frequency 100 Hz | IEC 60250 |
| 0.0240 @Frequency 1.00e+6 Hz | 0.0240 @Frequency 1.00e+6 Hz | IEC 60250 | |
| Comparative Tracking Index | 200 V | 200 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 7.00 μm/m-°C | 3.89 μin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 24.0 μm/m-°C | 13.3 μin/in-°F | ISO 11359-2 |
| Specific Heat Capacity | 1.50 J/g-°C | 0.359 BTU/lb-°F | Internal |
| Thermal Conductivity | 0.320 W/m-K | 2.22 BTU-in/hr-ft2-°F | Internal |
| Melting Point | 355 °C | 671 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 295 °C | 563 °F | ISO 75-1, -2 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | UL94 |
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | UL94 | |
| Oxygen Index | 45.0 % | 45.0 % | ISO 4589 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 30.0 °C | 68.0 - 86.0 °F | |
| 80.0 - 120 °C | 176 - 248 °F | Cavity temperature | |
| 275 °C | 527 °F | Ejection temperature; Internal | |
| Feed Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Zone 1 | 355 - 365 °C | 671 - 689 °F | |
| Zone 2 | 360 - 370 °C | 680 - 698 °F | |
| Zone 3 | 360 - 370 °C | 680 - 698 °F | |
| Zone 4 | 360 - 370 °C | 680 - 698 °F | |
| Die Temperature | 360 - 370 °C | 680 - 698 °F | |
| Melt Temperature | 360 - 370 °C | 680 - 698 °F | |
| 360 - 370 °C | 680 - 698 °F | ||
| 365 °C | 689 °F | Optimum | |
| Mold Temperature | 80.0 °C | 176 °F | Optimum |
| 40.0 - 150 °C | 104 - 302 °F | ||
| Drying Temperature | >= 150 °C | >= 302 °F | |
| Dry Time | 3.00 hour | 3.00 hour | |
| Moisture Content | 0.0100 % | 0.0100 % | Necessary low maximum residual |
| Injection Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |
| Hold Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |
| Back Pressure | 3.00 MPa | 435 psi | |