- 彎曲模量 [MPa]: 10.5
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 175 MPa | 25400 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 3.30 % | 3.30 % | 5mm/min; ISO 527-2/1A |
| Flexural Strength | 170 MPa | 24700 psi | ISO 178 |
| Flexural Modulus | 10.5 GPa | 1520 ksi | ISO 178 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 2.50 @Frequency 1.00e+6 Hz | 2.50 @Frequency 1.00e+6 Hz | IEC 60250 |
| 3.76 @Frequency 2.05e+9 Hz | 3.76 @Frequency 2.05e+9 Hz | IPC TM-650 2.5.5.13 | |
| Dissipation Factor | 0.00300 @Frequency 2.05e+9 Hz | 0.00300 @Frequency 2.05e+9 Hz | IPC TM-650 2.5.5.13 |
| 0.0159 @Frequency 1.00e+6 Hz | 0.0159 @Frequency 1.00e+6 Hz | IEC 60250 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 319 °C | 606 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 275 °C | 527 °F | ISO 75-1, -2 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | UL94 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 30.0 °C | 68.0 - 86.0 °F | |
| 80.0 - 120 °C | 176 - 248 °F | Cavity temperature | |
| Feed Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Zone 1 | 320 - 330 °C | 608 - 626 °F | |
| Zone 2 | 335 - 345 °C | 635 - 653 °F | |
| Zone 3 | 335 - 345 °C | 635 - 653 °F | |
| Zone 4 | 335 - 345 °C | 635 - 653 °F | |
| Die Temperature | 335 - 345 °C | 635 - 653 °F | |
| Melt Temperature | 325 - 345 °C | 617 - 653 °F | |
| Drying Temperature | 150 °C | 302 °F | |
| Dry Time | 3.00 hour | 3.00 hour | |
| Moisture Content | 0.0100 % | 0.0100 % | Necessary low maximum residual |
| Injection Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |
| Hold Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |
| Back Pressure | 3.00 MPa | 435 psi | |