- 熔體流動速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.886
- 缺口沖擊強度: 1.07
- 拉伸強度 [MPa]: 32.0
- 彎曲模量 [MPa]: 1.52
- 熱變形溫度 [℃]: 99.0
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.886 - 0.926 g/cc | 0.0320 - 0.0335 lb/in3 | ASTM D1505 |
| Water Absorption | <= 0.010 % | <= 0.010 % | 24 hours; ASTM D570 |
| Linear Mold Shrinkage | 0.010 - 0.025 cm/cm | 0.010 - 0.025 in/in | ASTM D955 |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM D638 |
| Flexural Modulus | 1.52 GPa | 220 ksi | ASTM D790A |
| Izod Impact, Notched | 1.07 J/cm @Diameter 3.17 mm | 2.00 ft-lb/in @Diameter 0.125 in | bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 99.0 °C | 210 °F | ASTM D648 |
| Optical Properties | Metric | English | Comments |
| Haze | 11 % @Thickness 1.27 mm | 11 % @Thickness 0.0500 in | plaque; ASTM D1003 |
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified |